Effect of ceramic powder fineness on mullite-zirconium ceramic properties

被引：0
作者：
G. P. Sedmale
A. V. Khmelev
I. É. Shperberga
机构：
[1] Riga Technical University,
[2] Institute of Silicate Materials,undefined
来源：
Refractories and Industrial Ceramics | 2011年 / 52卷
关键词：
mullite-zirconium ceramic; illite clay; grinding; particle size;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Results are provided for a study of the development of high-temperature mullite-zirconium ceramic with use of activated ceramic powders prepared by grinding for different times with addition of illite clay, and from pure oxide powders. It is shown that increased activity and amorphicity of ground particles considerably promotes formation of mullite phase at 1200°C, and also transition of the monoclinic modification of ZrO2 to tetragonal, particularly with an increase in firing temperature. It is proposed that as a result of rapid “freezing” the structure retains the high-temperature modification of ZrO2, having a tendency with slow ceramic cooling to transform into the monoclinic modification.
引用
收藏
页码：35 / 40
页数：5
相关论文
共 24 条
  • [1] Sedmali G. P.(2008)Formation of ceramic in the system Al2O3–SiO2–ZrO2 in the presence of mineralizers Ogneupory Tekhn. Keram. 5 18-23
  • [2] Sperberger I. É.(2006)Formation of high-temperature crystalline phases in ceramics from illite clay and dolomite J. Eur. Ceram. Soc. 26 3351-3355
  • [3] Khmelev A. V.(2008)Role of mechanical activation of precursors in solid-state processing of nano-structured mullite phase J. of Alloys and Compounds 450 421-425
  • [4] Sedmale G(2001)Fabrication of mullite composites by cyclic infiltration and reaction sintering Materials Science and Engineering A 298 179-186
  • [5] Sperberga I(2003)Anisotropic grain growth of mullite in high-energy ball milling powders doped with transition metal oxides, J. Eur. Ceram. Soc. 23 2247-2256
  • [6] Sedmalis U(2006)Alumina-mullite ceramics for structuring applications Ceramics International 32 369-375
  • [7] Behmanesh N(2003)The effect of mullite on mechanical properties and thermal shock behavior of alumina-mullite refractory materials Ceramics International 29 183-188
  • [8] Manesh SH(2009)Use of wide-angle x-ray diffraction to measure shape and size of dispersed colloidal particles J. of Colloid and Interface Science 338 105-110
  • [9] Lin Y(2008)Growth of textured mullite fibers using a quadrupole lamp furnace, J. Eur. Ceram. Soc. 28 455-463
  • [10] Yi Chen(2008)Thermal shock behavior of dense mullite-zirconia composites obtained by two processing routes Ceramics International 34 2017-2024
123