Influence of Ti addition on the hydrogen induced cracking of API 5L X70 hot-rolled pipeline steel in acid sour media

被引：0
|
作者：
Joonoh Moon
Chulbong Park
Seong-Ju Kim
机构：
[1] Korea Institute of Materials Science,Ferrous Alloy Department, Advanced Metallic Materials Division
[2] Hyundai Steel Company,Sheet Products Design Team, Technical Research Center
来源：
Metals and Materials International | 2012年 / 18卷
关键词：
metals; rolling; corrosion; precipitation; hydrogen;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, Hydrogen Induced Cracking (HIC) testing of high strength API 5L grade X70 linepipe hot rolled steel containing Ti was performed to investigate the effects of (Nb, Ti, V)(C, N) particles on HIC susceptibility. By controlling chemical composition and hot rolling parameters, experimental steel with Bainitic ferrite and Bainite microstructures was fabricated. HIC testing was carried out within an acidic condition (pH=2.7±0.1) according to NACE standards with test results showing cracking propagated along coarse (Nb, Ti, V)(C, N) particles at mid-thickness. This is mainly due to centerline segregation and hydrogen blistering between matrix and coarse (Nb, Ti, V)(C, N) particles without external stress.
引用
收藏
页码：613 / 617
页数：4
相关论文
共 29 条
  • [1] Influence of Ti addition on the hydrogen induced cracking of API 5L X70 hot-rolled pipeline steel in acid sour media
    Moon, Joonoh
    Park, Chulbong
    Kim, Seong-Ju
    METALS AND MATERIALS INTERNATIONAL, 2012, 18 (04) : 613 - 617
  • [2] Role of Ca treatment in hydrogen induced cracking of hot rolled API pipeline steel in acid sour media
    Moon, Joonoh
    Kim, Seong-Ju
    Lee, Changhee
    METALS AND MATERIALS INTERNATIONAL, 2013, 19 (01) : 45 - 48
  • [3] Role of Ca treatment in hydrogen induced cracking of hot rolled API pipeline steel in acid sour media
    Joonoh Moon
    Seong-Ju Kim
    Changhee Lee
    Metals and Materials International, 2013, 19 : 45 - 48
  • [4] Microstructure and texture evolution in warm rolled API 5L X70 pipeline steel for sour service application
    Omale, J. I.
    Ohaeri, E. G.
    Szpunar, J. A.
    Arafin, M.
    Fateh, F.
    MATERIALS CHARACTERIZATION, 2019, 147 : 453 - 463
  • [5] Hydrogen induced cracking susceptibility of API 5L X70 pipeline steel in relation to microstructure and crystallographic texture developed after different thermomechanical treatments
    Ohaeri, Enyinnaya
    Szpunar, Jerzy
    Fazeli, Fateh
    Arafin, Muhammad
    MATERIALS CHARACTERIZATION, 2018, 145 : 142 - 156
  • [6] Effect of post-processing heat treatment on hydrogen embrittlement susceptibility of API 5L X70 pipeline steel
    Yadav, Sandeep
    Jack, Tonye Alaso
    Davani, Reza Khatib Zadeh
    Ohaeri, Enyinnaya
    Szpunar, Jerzy
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2022, 199
  • [7] Reliability estimation of pressurized API 5L X70 pipeline steel under longitudinal elliptical corrosion defect
    Zelmati, Djamel
    Ghelloudj, Oualid
    Amirat, Abdelaziz
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2017, 90 (9-12) : 2777 - 2783
  • [8] Reliability estimation of pressurized API 5L X70 pipeline steel under longitudinal elliptical corrosion defect
    Djamel Zelmati
    Oualid Ghelloudj
    Abdelaziz Amirat
    The International Journal of Advanced Manufacturing Technology, 2017, 90 : 2777 - 2783
  • [9] Influence of precipitation behavior on mechanical properties and hydrogen induced cracking during tempering of hot-rolled API steel for tubing
    Moon, Joonoh
    Choi, Jongmin
    Han, Seong-Kyung
    Huh, Sungyul
    Kim, Seong-Ju
    Lee, Chang-Hoon
    Lee, Tae-Ho
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 652 : 120 - 126
  • [10] Sour corrosion performance and sensitivity to hydrogen induced cracking in the X70 pipeline steel: Effect of microstructural variation and pearlite percentage
    Anijdan, S. H. Mousavi
    Sabzi, M.
    Park, N.
    Lee, Unhae
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2022, 199
123