Experimental Investigations on the Critical Current of the Jointed Bi-2223/Ag HTS Tapes

This paper summarizes the experimental investigations on the critical current of two jointed Bi-2223/Ag superconducting tapes connected by Sn63Ag2Pb solder. Different lap lengths of contact surface were studied. The joint resistance was measured to be in the range of 0.059∼0.76 μΩ, and the critical current of the jointed Bi-2223/Ag HTS tapes was measured with different charging rates using standard four-point-method in a zero-applied magnetic field applying 1 μV/cm criterion. The experimental results showed that the longer the lap length was, the smaller the joint resistance was and the nearer the critical current approached that of Bi-2223/Ag superconducting short-sample. On the other hand, the critical current decreased with the increasing of the charging rate.