Synthesis of In2O3 Thin Films from Indium Thin Film by Hot-Water Oxidation Method

被引：0
作者：
Subramani Shanmugan
Devarajan Mutharasu
机构：
[1] Universiti Sains Malaysia (USM),Nano Optoelectronics Research Laboratory, School of Physics
来源：
Metallurgical and Materials Transactions A | 2012年 / 43卷
关键词：
Oxygen Vacancy; In2O3; Indium Oxide; Soda Lime Glass Substrate; In2O3 Film;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Radio-frequency (RF)-sputtered indium thin films were prepared and processed in ultrapure water at 368 K (95 °C) for various time durations. The processed samples were poor in crystalline quality and indexed as cubic phase for the samples processed for more than 12 hours. A rhombohedral to cubic phase was also observed. Photoluminescence (PL) and Raman spectra showed few dominant peaks at ~385, ~515, and ~675 and at ~203 and 495 cm−1 as oxygen deficient cubic In2O3 with nanostructured In2O3, respectively.
引用
收藏
页码：6 / 9
页数：3
相关论文
共 122 条
[1]  
Xu J.(2008)undefined Mater. Lett. 62 1363-65
[2]  
Chen Y.(1983)undefined Thin Solid Films 102 1-46
[3]  
Shen J.(2000)undefined Sol. Energy Mater. Sol. Cells 60 201-62
[4]  
Chopra K.L.(1997)undefined Thin Solid Films 305 116-23
[5]  
Major S.(2003)undefined Surf. Coat. Technol. 172 242-50
[6]  
Pandya D.K.(2002)undefined Thin Solid Films 411 17-22
[7]  
Granquist C.G.(2004)undefined Sens. Actuators B 97 256-65
[8]  
Ajili A.N.H.(2004)undefined Renew Energ. 29 1671-76
[9]  
Bayliss S.C.(1996)undefined Thin Solid Films 279 1-3
[10]  
Girtan M.(1996)undefined J. Appl. Phys. 79 8521-30
12345678910