Microstructure and mechanical properties of 316L stainless steel joints brazed by BNi-7 alloyed with different Cu content

被引:0
作者
Youqiong Qin
Wenxiang Jiang
机构
[1] Shanghai University of Engineering Science,School of Material Engineering
来源
Welding in the World | 2019年 / 63卷
关键词
BNi-7 alloyed with Cu; Brazing; 316L stainless steel; Microstructure; Shear strength;
D O I
暂无
中图分类号
学科分类号
摘要
New Ni-Cr-P-Cu brazing alloys were produced in a vacuum melting furnace by adding different amount of Cu content to traditional Cu-free BNi-7 brazing alloy. 316L stainless steel was brazed with the new brazing alloy and compared with that of traditional BNi-7 brazing alloy. The physical characteristics of these brazing alloys were analyzed by DSC (differential scanning calorimetry). The microstructures of the brazing alloys and brazed joints were investigated by SEM (scanning electron microscopy) and EDS (energy-dispersive spectrometer). The shear strength and hardness of the brazed joints were also studied. The results showed that the liquidus temperature of brazing alloys decreased with the increasing Cu content. There existed two phases (primary phase (ductile α-Ni) and eutectic phase (brittle Ni3P-Ni)) in the brazing alloy and in the middle of the brazed joints. The amount of brittle phases decreased with the increasing Cu content. The shear strength at room temperature of the new brazed joint was 118 MPa for BNi-7 alloyed with 9 wt.% Cu, which was higher than that of the traditional BNi-7 brazing alloy that exhibited a shear strength of 96 MPa.
引用
收藏
页码:1469 / 1475
页数:6
相关论文
共 50 条
[41]   Microstructure and mechanical properties of the austenitic stainless steel 316L fabricated by gas metal arc additive manufacturing [J].
Chen, Xiaohui ;
Li, Jia ;
Cheng, Xu ;
He, Bei ;
Wang, Huaming ;
Huang, Zheng .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 703 :567-577
[42]   Effects of laser power on the microstructure and mechanical properties of 316L stainless steel prepared by selective laser melting [J].
Zheng, Zeng ;
Wang, Lianfeng ;
Yan, Biao .
INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2017, 31 (16-19)
[43]   Enhanced sintering, microstructure evolution and mechanical properties of 316L stainless steel with MoSi2 addition [J].
Akhtar, Farid ;
Ali, Liaqat ;
Feng Peizhong ;
Shah, Jawad Ali .
JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (35) :8794-8797
[44]   Effect of laser rescanning on microstructure and mechanical properties of direct energy deposited AISI 316L stainless steel [J].
Kim, Tae Hwan ;
Yun, Gyeong ;
Jeon, Jong ;
Lee, Ki Yong ;
Shim, Sik ;
Lee, Wookjin .
SURFACE & COATINGS TECHNOLOGY, 2021, 405
[45]   Effect of building orientation on weld characteristics of additively manufactured 316L stainless steel: Microstructure and mechanical properties [J].
Khedr, Mahmoud ;
Elsayed, Mohamed ;
Jaskari, Matias ;
Abdel-Aleem, Hamed A. ;
Gaafer, A. M. ;
Hamada, Atef .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2024, 913
[46]   Mechanical, Microstructure, and Corrosion Characterization of Dissimilar Austenitic 316L and Duplex 2205 Stainless-Steel ATIG Welded Joints [J].
Touileb, Kamel ;
Hedhibi, Abdeljlil Chihaoui ;
Djoudjou, Rachid ;
Ouis, Abousoufiane ;
Bensalama, Abdallah ;
Ibrahim, Albaijan ;
Abdo, Hany S. ;
Ahmed, Mohamed M. Z. .
MATERIALS, 2022, 15 (07)
[47]   Interfacial Microstructure and Mechanical Properties of TC4 Titanium Alloy/316L Stainless Steel Joint Brazed with Ag70.5Cu27.5Ti2 Filler Metal [J].
Yang, Mei ;
Wu, Xin ;
Gong, Xiufang ;
Li, Yang ;
Nie, Liping ;
Yang, Honglang ;
Li, Shuang .
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2021, 74 (08) :1907-1916
[48]   Microstructure and Properties of Plasma Arc Powder Additive Manufactured 316L Stainless Steel with Different Cooling Conditions [J].
Zhao Y. ;
Wang Z. ;
Zhao J. ;
He Z. ;
Li S. ;
Zhang H. .
Xiyou Jinshu/Chinese Journal of Rare Metals, 2021, 45 (09) :1062-1069
[49]   Interfacial Microstructure and Mechanical Properties of TC4 Titanium Alloy/316L Stainless Steel Joint Brazed with Ag70.5Cu27.5Ti2 Filler Metal [J].
Mei Yang ;
Xin Wu ;
Xiufang Gong ;
Yang Li ;
Liping Nie ;
Honglang Yang ;
Shuang Li .
Transactions of the Indian Institute of Metals, 2021, 74 :1907-1916
[50]   Interface behaviors and mechanical properties of diffusion bonded 45 steel/ additive manufactured 316L steel joints [J].
Xu, Ruiwen ;
Zhu, Yi ;
Li, Bingnan ;
Yang, Huayong ;
Zhang, Chao .
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 30 :1279-1287