Comparative tribological behavior of friction composites containing natural graphite and expanded graphite

被引：0
作者：
Hongyun Jin
Keke Zhou
Zhengjia Ji
Xiaocong Tian
Ying Chen
Luhua Lu
Yazhou Ren
Chunhui Xu
Shanshan Duan
Jiangyu Li
Shu-en Hou
机构：
[1] China University of Geosciences,Faculty of Materials Science and Chemistry
[2] University of Washington,Department of Mechanical Engineering
来源：
Friction | 2020年 / 8卷
关键词：
natural graphite; expanded graphite; tribological behavior; wear mechanism;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, expanded graphite and natural graphite were introduced into resin-based friction materials, and the tribological behavior of the composites was investigated. The tribo-performance of the two friction composites was evaluated using a constant speed friction tester. The results showed that the expanded graphite composite (EGC) displayed better lubricity in both the fading and the recovery processes. The wear rate of the EGC decreased by 22.43% more than that of the natural graphite composite (NGC). In the fading process, and the EGC enhanced the stability of the coefficient of friction. The recovery maintenance rate of the NGC was 4.66% higher than that of the EGC. It can be concluded that expanded graphite plays an important role in the formation of a stable contact plateau and can effectively reduce the wear.
引用
收藏
页码：684 / 694
页数：10
相关论文
共 136 条
[1]  
Martinez A M(2016)Towards a better understanding of the reaction between metal powders and the solid lubricant Sb Wear 348–349 27-42
[2]  
Echeberria J(2018)S Tribol Int 120 58-69
[3]  
Faig J J(2018) in a low-metallic brake pad at high temperature J Tribol 140 032003-358
[4]  
Zhang Y Y(2018)Thermocleavable friction modifiers for controlled release in lubricants Tribol Int 123 349-160
[5]  
Man K N(2016)Tribological behaviors of polymer-based hybrid nanocomposite brake pad Lubricants 4 5-22
[6]  
Luo S J(2015)Preparation of a mica- organic hybrid solid lubricant and characterization of its lubrication mechanisms Mater Des 77 149-410
[7]  
Shough A M(2016)The role of solid lubricants for brake friction materials Wear 358–359 17-1482
[8]  
Schilowitz A(2016)Effects of solid lubricants, load, and sliding speed on the tribological behavior of silica reinforced composites using design of experiments Compos Part B: Eng 94 399-124
[9]  
Dierolf M(2010)Comparative performance evaluation of NAO friction materials containing natural graphite and thermo-graphite Wear 268 1472-909
[10]  
Uhrich K E(2016)Design and development of high performance tribo-composites based on synergism in two solid lubricants Theor Appl Fract Mech 85 113-96
12345678910