Effect of additives on the firing temperature of a current-conducting composite

被引：0
|
作者：
S. P. Rodtsevich
G. G. Mamedova
机构：
[1] Academy of Sciences of Belarus,Institute of General and Inorganic Chemistry
来源：
Glass and Ceramics | 1997年 / 54卷
关键词：
Uric Acid; Precious Metal; Firing Temperature; Heating Element; Indium Oxide;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A study was undertaken to see how sulfuric acid and alkalis would affect the firing temperature of a current-conducting composite. It was found that sulfuric acid, when added to the composite, acts to depress the firing temperature, and the alkali causes it to rise. The proposed current-conducting coatings will extend the service life of heating elements, improve their efficiency, and exclude the use of the precious metals.
引用
收藏
页码：96 / 97
页数：1
相关论文
共 34 条
  • [11] The effect of mineralogy, microstructure and firing temperature on the effective thermal conductivity of traditional hot processing ceramics
    Allegretta, Ignazio
    Eramo, Giacomo
    Pinto, Daniela
    Hein, Anno
    APPLIED CLAY SCIENCE, 2017, 135 : 260 - 270
  • [12] Effect of firing temperature on the water permeability of SiO2-ZrO2 membranes for nanofiltration
    Puthai, Waravut
    Kanezashi, Masakoto
    Nagasawa, Hiroki
    Wakamura, Katsumi
    Ohnishi, Hiroshi
    Tsuru, Toshinori
    JOURNAL OF MEMBRANE SCIENCE, 2016, 497 : 348 - 356
  • [13] Effect of firing temperature on the properties of sol-gel films of the CuO-TiO2 system
    A. B. Atkarskaya
    M. I. Zaitseva
    Glass and Ceramics, 2007, 64 : 349 - 353
  • [14] Effect of intermediate ceramics and firing temperature on bond strength between tetragonal zirconia polycrystal and veneering ceramics
    Matsumoto, Naoya
    Yoshinari, Masao
    Takemoto, Shinji
    Hattori, Masayuki
    Kawada, Eiji
    Oda, Yutaka
    DENTAL MATERIALS JOURNAL, 2013, 32 (05) : 734 - 743
  • [15] Effect of firing temperature on the properties of sol-gel films of the CuO-TiO2 system
    Atkarskaya, A. B.
    Zaitseva, M. I.
    GLASS AND CERAMICS, 2007, 64 (9-10) : 349 - 353
  • [16] The effect of Si content, firing temperature, and urea additive on the properties of nitride-bonded SiC refractories
    Nourbakhsh, A. A.
    Golestani-fard, F.
    Rezaie, H. R.
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2007, 48 (05) : 383 - 386
  • [17] The effect of Si content, firing temperature, and urea additive on the properties of nitride-bonded SiC refractories
    A. A. Nourbakhsh
    F. Golestani-fard
    H. R. Rezaie
    Refractories and Industrial Ceramics, 2007, 48 : 383 - 386
  • [18] Effect of Firing Temperature and Reducing Gas Composition during Low-Temperature Reduction of Nanocrystalline Fe2O3
    M. BAHGAT
    M.H. KHEDR
    M.I. NASR
    E.K. SEDEEK
    Metallurgical and Materials Transactions B, 2007, 38 : 5 - 11
  • [19] Effect of Firing Temperature on Mechanical Properties of Al2O3-C Sensor for Continuous Measurement of Molten Steel Temperature
    Zhang, Jiu
    Mei, Guohui
    Zhao, Shumao
    Xie, Zhi
    ISIJ INTERNATIONAL, 2014, 54 (03) : 553 - 558
  • [20] Effect of the firing temperature and the added MgO on the reduction swelling index of the pellet with low SiO2 content
    Qing, G.
    Wu, K.
    Tian, Y.
    An, G.
    Yuan, X.
    Xu, D.
    Huang, W.
    IRONMAKING & STEELMAKING, 2018, 45 (01) : 83 - 89
1234