Nanoindentation of regenerated cellulose fibres

被引：0
作者：
Wolfgang Gindl
Johannes Konnerth
Thomas Schöberl
机构：
[1] BOKU-Vienna,Department of Materials Science and Process Engineering
[2] WOOD K PLUS,Competence Centre for Wood Composites and Wood Chemistry
[3] Austrian Academy of Sciences,Erich Schmid Institute for Materials Science
来源：
Cellulose | 2006年 / 13卷
关键词：
Elastic modulus; Hardness; Lyocell; Nanoindentation; Regenerated cellulose fibre; Viscose;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Nanoindentation was performed on cross sections of regenerated cellulose fibres with different structure and properties. Same as in single-fibre tensile tests, the elastic modulus of lyocell was higher than the elastic modulus of viscose. However, in spite of its tensile strength being twice as high as viscose, the hardness of lyocell was 15% lower than viscose. The overall degree of orientation of cellulose chains being higher in lyocell than in viscose, it is proposed that reduced lateral bonding in lyocell is the reason for the low hardness measured by nanoindentation compared to viscose.
引用
收藏
页码：1 / 7
页数：6
相关论文
共 50 条
[41]   Compact Spinning Research for Regenerated Cellulose and Synthetic Yarns [J].
Altas, Sevda ;
Kadoglu, Huseyin .
TEKSTILEC, 2009, 52 (10-12) :306-311
[42]   Swelling and dissolution mechanisms of regenerated Lyocell cellulose fibers [J].
Cyril Chaudemanche ;
Patrick Navard .
Cellulose, 2011, 18 :1-15
[43]   Swelling and dissolution mechanisms of regenerated Lyocell cellulose fibers [J].
Chaudemanche, Cyril ;
Navard, Patrick .
CELLULOSE, 2011, 18 (01) :1-15
[44]   THE PERFORMANCE PROPERTIES OF THE FABRICS PRODUCED FROM CUPRO AND SOME OTHER REGENERATED CELLULOSE FIBERS [J].
Dirgar, Esra .
TEKSTIL VE KONFEKSIYON, 2017, 27 (02) :139-144
[45]   Investigation of nanoindentation mechanical properties for cellulose/PHA nanocomposite using molecular dynamics simulation [J].
Liu, Feng ;
Wu, Ruoyu ;
Zhu, Yuan ;
Zou, Rui ;
Ning, Huiming ;
Hu, Ning .
COMPOSITES COMMUNICATIONS, 2025, 53
[46]   High modulus regenerated cellulose fiber-reinforced cellulose acetate butyrate biocomposites [J].
Carrillo, F. ;
Martin, G. ;
Lopez-Mesas, M. ;
Colom, X. ;
Canavate, J. .
JOURNAL OF COMPOSITE MATERIALS, 2011, 45 (17) :1733-1740
[47]   Nanoindentation of embedded particles [J].
Slagter, Alejandra ;
Everaerts, Joris ;
Mortensen, Andreas .
JOURNAL OF MATERIALS RESEARCH, 2023, 38 (06) :1694-1705
[48]   Future of nanoindentation in archaeometry [J].
Faisal, Nadimul Haque ;
Ahmed, Rehan ;
Goel, Saurav ;
Cross, Graham .
JOURNAL OF MATERIALS RESEARCH, 2018, 33 (17) :2515-2532
[49]   Nanoindentation of clay colloidosomes [J].
Mallikarjunachari, G. ;
Nallamilli, Trivikram ;
Ravindran, Parag ;
Basavaraj, Madivala G. .
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2018, 550 :167-175
[50]   Dissolving pulp from eucalyptus sawdust for regenerated cellulose products [J].
Evangelina Vallejos, Maria ;
Viviana Olmos, Graciela ;
Claudia Taleb, Maria ;
Esteban Felissia, Fernando ;
Vanesa Ehman, Nanci ;
Peresin, Maria Soledad ;
Cristina Area, Maria ;
Graciela Maximino, Mirtha .
CELLULOSE, 2022, 29 (08) :4645-4659
12345