Brazing of zirconia with AgCuTi and SnAgTi active filler metals

被引：0
|
作者：
T. H. Chuang
M. S. Yeh
Y. H. Chai
机构：
[1] National Taiwan University,the Institute of Materials Science and Engineering
[2] Chung-Hua University,the Department of Mechanical Engineering
[3] NEC Electronics,the Micro Design and Development Division
[4] Inc.,undefined
来源：
Metallurgical and Materials Transactions A | 2000年 / 31卷
关键词：
Contact Angle; Material Transaction; Exothermic Peak; Interfacial Reaction; Filler Metal;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The self-brazing of partially stabilized zirconia using Ag27Cu3Ti and Sn10Ag4Ti active filler metals is investigated. It was shown that the contact angles of Ag27Cu3Ti and Sn10Ag4Ti on zirconia decreased with the increase of brazing temperature and remained constant at about 34 deg and 44 deg above 900 °C, respectively. The flexural strengths were 227 and 137 MPa for ZrO2/Ag27Cu3Ti/ZrO2 and ZrO2/Sn10Ag4Ti/ZrO2, respectively, after brazing at 900 °C for 10 minutes.
引用
收藏
页码：1591 / 1597
页数：6
相关论文
共 50 条
  • [31] Micro–nano filler metal foil on vacuum brazing of SiCp/Al composites
    Peng Wang
    Zeng Gao
    Jitai Niu
    Applied Physics A, 2016, 122
  • [32] Joining of Si3N4 to 1.25Cr0.5Mo steel using rapidly solidified CuNiTiB foils as brazing filler metals
    Wan, CQ
    Xiong, HP
    Zhou, ZF
    WELDING JOURNAL, 1997, 76 (12) : S522 - S525
  • [33] A Research on Interfacial Reaction of Brazing Joint of Alumina Ceramics to Metals
    Ma, Xiangdong
    Wang, Xinyang
    Li, Jiwen
    Wei, Shizhong
    PRICM 7, PTS 1-3, 2010, 654-656 : 2732 - +
  • [34] Influence of sulphur on the microstructure and properties of Ag-Cu-Zn brazing filler metal
    Chen, Y.
    Yun, D.
    Sui, F.
    Long, W.
    Zhang, G.
    Liu, S.
    MATERIALS SCIENCE AND TECHNOLOGY, 2013, 29 (10) : 1267 - 1271
  • [35] Interface Behavior of Brazing between Zr-Cu Filler Metal and SiC Ceramic
    Zhou, Bofang
    Li, Taohua
    Zhang, Hongxia
    Hou, Junliang
    CRYSTALS, 2021, 11 (07)
  • [36] Computer simulation of wetting and flowing behaviors of filler metal during laser brazing process
    Saida, Kazuyoshi
    Song, Woohyun
    Nishimoto, Kazutoshi
    ADVANCED WELDING AND MICRO JOINING / PACKAGING FOR THE 21ST CENTURY, 2008, 580-582 : 271 - +
  • [37] Diffusion brazing of stainless steels influence of Ni-B filler alloy composition
    Ivannikov, Alexander Alexandrovich
    Penyaz, Milena Alexeevna
    Dzhumaev, Pavel Sergeevich
    Bachurina, Diana Mikhailovna
    Sevriukov, Oleg Nikolaevich
    WELDING IN THE WORLD, 2021, 65 (02) : 317 - 328
  • [38] Diffusion brazing of stainless steels influence of Ni-B filler alloy composition
    Alexander Alexandrovich Ivannikov
    Milena Alexeevna Penyaz
    Pavel Sergeevich Dzhumaev
    Diana Mikhailovna Bachurina
    Oleg Nikolaevich Sevriukov
    Welding in the World, 2021, 65 : 317 - 328
  • [39] A Study on the Wetting Behaviour of Al-Si-Zn Brazing Filler on AA7075 and AR500 Surface
    Muhamed, Mohd Najib
    Omar, Mohd Zaidi
    Abdullah, Shahrum
    Sajuri, Zainuddin
    Zamri, Wan Fathul Hakim Wan
    Selamat, Zainal Ariffin
    JURNAL KEJURUTERAAN, 2020, 32 (01): : 113 - 119
  • [40] The interfacial reaction between diamond grit and Ni-based brazing filler metal
    Lee, ChangHun
    Ham, JongOh
    Song, MinSeok
    Lee, ChiHwan
    MATERIALS TRANSACTIONS, 2007, 48 (04) : 889 - 891
12345