Brazing of zirconia with AgCuTi and SnAgTi active filler metals

被引：0
|
作者：
T. H. Chuang
M. S. Yeh
Y. H. Chai
机构：
[1] National Taiwan University,the Institute of Materials Science and Engineering
[2] Chung-Hua University,the Department of Mechanical Engineering
[3] NEC Electronics,the Micro Design and Development Division
[4] Inc.,undefined
来源：
Metallurgical and Materials Transactions A | 2000年 / 31卷
关键词：
Contact Angle; Material Transaction; Exothermic Peak; Interfacial Reaction; Filler Metal;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The self-brazing of partially stabilized zirconia using Ag27Cu3Ti and Sn10Ag4Ti active filler metals is investigated. It was shown that the contact angles of Ag27Cu3Ti and Sn10Ag4Ti on zirconia decreased with the increase of brazing temperature and remained constant at about 34 deg and 44 deg above 900 °C, respectively. The flexural strengths were 227 and 137 MPa for ZrO2/Ag27Cu3Ti/ZrO2 and ZrO2/Sn10Ag4Ti/ZrO2, respectively, after brazing at 900 °C for 10 minutes.
引用
收藏
页码：1591 / 1597
页数：6
相关论文
共 50 条
  • [21] BRAZING OF SILICON-NITRIDE AND STEEL WITH CU-BASED FILLER METALS - MECHANISM AND RESIDUAL-STRESS IN ITS JOINTS
    GAO, MN
    BAO, FH
    INTERFACES II, 1995, 189- : 399 - 404
  • [22] Wetting Behavior of a Novel Al-Si-Ti Active Brazing Filler Metal Foil on Aluminum Matrix Composite
    Zhang, Guifeng
    Su, Wei
    Zhang, Jianxun
    Suzumura, Akio
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (07) : 1982 - 1994
  • [23] Wetting Behavior of a Novel Al-Si-Ti Active Brazing Filler Metal Foil on Aluminum Matrix Composite
    Guifeng Zhang
    Wei Su
    Jianxun Zhang
    Akio Suzumura
    Journal of Materials Engineering and Performance, 2013, 22 : 1982 - 1994
  • [24] Comparative analysis of the brazing mechanism and wear characteristics of brazed diamond abrasive with Zr-alloyed Cu-based filler metals
    Cui, Bing
    Yan, Peipei
    Du, Quanbin
    Jiang, Xue
    Zhang, Liyan
    Tong, Baohong
    DIAMOND AND RELATED MATERIALS, 2024, 141
  • [25] Wettability for understanding the behaviour of new filler materials for sinter-brazing
    Galan-Salazar, A.
    Campos, M.
    Torralba, J. M.
    Kjellen, L.
    Mars, O.
    POWDER METALLURGY, 2017, 60 (02) : 97 - 104
  • [26] Diode laser brazing of aluminium alloy to steels with aluminium filler metal
    Saida, K
    Song, W
    Nishimoto, K
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2005, 10 (02) : 227 - 235
  • [27] Carbothermal reduction reaction enhanced wettability and brazing strength of AgCuTi-SiO2f/SiO2 system
    Sun, Zhan
    Cao, Yu
    Zhang, Lixia
    Feng, Jicai
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2020, 40 (04) : 1488 - 1495
  • [28] High-Entropy Brazing Filler Metal Based on NiCoCrPdGe System for Brazing Nickel Superalloys, Metallofiz. Noveishie TekhnoL
    Voronov, V. V.
    Kovalchuk, P. V.
    METALLOPHYSICS AND ADVANCED TECHNOLOGIES, 2023, 45 (03) : 387 - 401
  • [29] Optimization of filler metal during superalloy-stainless steel arc brazing
    Fan, Chenglei
    Lin, Sanbao
    Yang, Chunli
    Song, Jianling
    RARE METALS, 2007, 26 : 36 - 40
  • [30] Study on Brazing of SiC Ceramics with Zr-Cu-Nb Filler Metal
    Zhang, Ziyi
    Cai, Yuchen
    Liu, Yanfang
    Feng, Keqin
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (16) : 8033 - 8043
12345