Dielectric and Ferroelectric Characterization of Na(Ta,Nb)O3 Solid Solution Ceramics

Ceramics in the Na(Ta1 − xNbx)O3 system were prepared by a solid state reaction approach, and their dielectric characteristics were evaluated together with the structures. The complete solid solution with orthorhombic structures was observed in the present system, and three supposed phase transitions at about 475, 580 and 650∘C were observed by DTA. Only one dielectric anomaly was observed at high temperature for x = 0.2 and 0.4, and alternative dielectric anomaly (a diffused dielectric peak) was observed around 170 and 380∘C for x = 0.6 and 0.8, respectively. The compositions of 0.6 and 0.8 are weakly ferroelectric and those of 0.2 and 0.4 are supposed to be antiferroelectric at room temperature.