Joining dense Si3N4 to porous Si3N4 by using an anorthite based glass-ceramic

被引：0
作者：
Jian Fang
Jie Zhang
ChunFeng Liu
LiangBo Sun
SongSong Guo
DongBao Wang
机构：
[1] Harbin Institute of Technology,School of Materials Science and Engineering
[2] Harbin Institute of Technology,Center of Analysis and Measurement
来源：
Science China Technological Sciences | 2020年 / 63卷
关键词：
Si; N; ceramic; glass-ceramic; joining; microstructure; shear strength;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This study focuses on the design, characterization and testing of a novel anorthite based glass-ceramic solder for joining dense Si3N4 and porous Si3N4 ceramic. It was found that the glass solder possesses a favorable wetting ability on two ceramic surfaces. Additionally, the influence of crystallization treatment on the microstructure and shear strength of joints was investigated. The results showed that CaAl2Si2O8 was the main product in the seam. After crystallization treatment, the crystallinitiy of the seam and shear strength of joints were improved obviously. The shear strength of joints after crystallization was 52 MPa at room temperature, and it increased to 59 MPa at 850°C. Finally, the joining mechanism of the dense Si3N4/glass-ceramic/porous Si3N4 bonded joints was proposed. Intergranular diffusion of elements was identified as the main mechanism of bonding in the interface of dense Si3N4/glass-ceramic. In the porous Si3N4 side, the bonding was achieved by infiltration that was controlled by capillarity and resistance of the viscous forces.
引用
收藏
页码：1538 / 1548
页数：10
相关论文
共 98 条
[1]  
Mazdiyasni K S(1978)Characterization of organosilicon-infiltrated porous reaction-sintered Si J Am Ceramic Soc 61 504-508
[2]  
West R(2005)N J Am Ceramic Soc 88 1030-1032
[3]  
David L D(2009)Synthesis of porous Si Ceramics Int 35 1699-1703
[4]  
Yang J F(2002)N Mater Sci Eng-A 335 26-31
[5]  
Zhang G J(2019) ceramics with rod-shaped pore structure J Alloys Compd 805 69-77
[6]  
Kondo N(2019)Dielectric and mechanical properties of porous Si Ceramics Int 45 23241-23247
[7]  
Xia Y(2016)N RSC Adv 6 63801-63808
[8]  
Zeng Y P(2013) ceramics prepared via low temperature sintering J Alloys Compd 559 152-157
[9]  
Jiang D(2012)Fabrication of porous anisotropic silicon nitride by using partial sinter-forging technique J Eur Ceramic Soc 32 1485-1489
[10]  
Kondo N(1996)Porous Si Scripta Mater 35 675-681
12345678910