Effect of Annealing Before Aging on Microstructure and Mechanical Properties of Mg-Gd-Y-Zn-Zr Alloy

被引：0
|
作者：
Chao Liu
Liang Liu
Jie Zheng
Zhaoming Yan
Zhimin Zhang
Qiang Wang
Xubin Li
Yong Xue
机构：
[1] North University of China,School of Materials Science and Engineering
来源：
Journal of Materials Engineering and Performance | 2022年 / 31卷
关键词：
annealing; aging; Mg-Gd-Y-Zn-Zr; mechanical properties; static recrystallization;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, in order to improve the elongation of Mg-9Gd-4Y-2Zn-0.5Zr alloy after aging, annealing treatment was introduced before aging. The alloy billet was subjected to 2 passes of cyclic expansion–extrusion with an asymmetrical cavity (CEE-AEC), then annealed and aged. Static recrystallization occurred during annealing, and the microstructure was refined. After annealing, the elongation of the sample reached the maximum, which is 7.4%, and the peak aging lagged due to dislocation consumption. Compared with the direct aging samples with the lowest elongation, aging after annealing could obtain more comprehensive mechanical properties. The ultimate tensile strength (UTS) was 362 MPa, and the elongation was 2.1%.
引用
收藏
页码：9829 / 9838
页数：9
相关论文
共 50 条
  • [21] Microstructure，Texture and Mechanical Properties of Mg-Gd-Y-Zn-Zr Sheet with Different Rolling Speed
    Wang X.
    Huang Y.
    Wang Q.
    Hu J.
    Li X.
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2023, 47 (07): : 934 - 941
  • [22] Effect of aging treatment on the precipitation transformation and age hardening of Mg-Gd-Y-Zn-Zr alloy
    Meng, Mu
    Zhang, Honglei
    Gao, Zhi
    Lei, Genxing
    Yu, Jianmin
    JOURNAL OF MAGNESIUM AND ALLOYS, 2023, 11 (12) : 4628 - 4643
  • [23] Microstructure and mechanical properties of rolled sheets of Mg-Gd-Y-Zn-Zr alloy: As-cast versus as-homogenized
    Xu, C.
    Zheng, M. Y.
    Xu, S. W.
    Wu, K.
    Wang, E. D.
    Kamado, S.
    Wang, G. J.
    Lv, X. Y.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 528 : 40 - 44
  • [24] Static Recrystallization Behavior of Mg-Gd-Y-Zn-Zr Alloy During Annealing Treatment
    Wu, Zeru
    Yu, Jianmin
    Zhang, Ziwei
    Hu, Hongbing
    Zhang, Zhimin
    JOM, 2022, 74 (07) : 2566 - 2576
  • [25] Microstructure and mechanical properties of Mg-Gd-Y-Zn-Zr alloy plates with different initial textures after hot rolling
    Chen, Han
    Hu, Zhang
    Han, Yu-xiang
    Chen, Tao
    Liu, Chu-ming
    Chen, Zhi-yong
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2024, 34 (06) : 1804 - 1816
  • [26] An alternating ageing-annealing process for enhancing strength and ductility of a Mg-Gd-Y-Zn-Zr alloy
    Zheng, Jie
    Chen, Zhe
    Yan, Zhaoming
    Zhang, Zhimin
    Xue, Yong
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 828
  • [27] Microstructure Evolution of Mg-Gd-Y-Zn-Zr Magnesium Alloy During Partial Remelting
    Tao, Jianquan
    Ji, Xinghua
    Zhang, Yanping
    Sun, Changjian
    Deng, Tianquan
    MATERIALS SCIENCE-MEDZIAGOTYRA, 2014, 20 (04): : 436 - 439
  • [28] Evolution of long-period stacking ordered phases and their effect on recrystallization in extruded Mg-Gd-Y-Zn-Zr alloy during annealing
    Xiao, Jianxiong
    Chen, Zhiyong
    Shao, Jianbo
    Chen, Tao
    Lin, Xia
    Liu, Chuming
    MATERIALS CHARACTERIZATION, 2020, 167
  • [29] Effect of ageing treatment on the precipitation behaviour of Mg-Gd-Y-Zn-Zr alloy
    Xu, C.
    Zheng, M. Y.
    Wu, K.
    Wang, E. D.
    Fan, G. H.
    Xu, S. W.
    Kamado, S.
    Liu, X. D.
    Wang, G. J.
    Lv, X. Y.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 550 : 50 - 56
  • [30] Microstructure and mechanical properties of Mg-Gd-Y-Zn-Zr alloy sheets processed by combined processes of extrusion, hot rolling and ageing
    Xu, C.
    Zheng, M. Y.
    Xu, S. W.
    Wu, K.
    Wang, E. D.
    Fan, G. H.
    Kamado, S.
    Liu, X. D.
    Wang, G. J.
    Lv, X. Y.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 559 : 844 - 851
12345