Effect of Annealing Before Aging on Microstructure and Mechanical Properties of Mg-Gd-Y-Zn-Zr Alloy

被引：0
作者：
Chao Liu
Liang Liu
Jie Zheng
Zhaoming Yan
Zhimin Zhang
Qiang Wang
Xubin Li
Yong Xue
机构：
[1] North University of China,School of Materials Science and Engineering
来源：
Journal of Materials Engineering and Performance | 2022年 / 31卷
关键词：
annealing; aging; Mg-Gd-Y-Zn-Zr; mechanical properties; static recrystallization;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, in order to improve the elongation of Mg-9Gd-4Y-2Zn-0.5Zr alloy after aging, annealing treatment was introduced before aging. The alloy billet was subjected to 2 passes of cyclic expansion–extrusion with an asymmetrical cavity (CEE-AEC), then annealed and aged. Static recrystallization occurred during annealing, and the microstructure was refined. After annealing, the elongation of the sample reached the maximum, which is 7.4%, and the peak aging lagged due to dislocation consumption. Compared with the direct aging samples with the lowest elongation, aging after annealing could obtain more comprehensive mechanical properties. The ultimate tensile strength (UTS) was 362 MPa, and the elongation was 2.1%.
引用
收藏
页码：9829 / 9838
页数：9
相关论文
共 297 条
[1]  
Zheng XW(2019)The Effect of Casting Speed on Microstructure, Microsegregation, and Mechanical Properties of High-Strength Mg-Nd-Zn-Zr Alloy J. Mater. Eng. Perform. 28 1753-1761
[2]  
Luo P(2014)Strengthening Precipitate, Thermal Stability, and Mechanical Properties of Melt-Spun Mg-8Gd-3Nd Alloy J. Mater. Eng. Perform. 23 250-254
[3]  
Dong J(2018)Evolution of LPSO Phases in a Mg-Zn-Y-Gd-Zr Alloy During Semi-Continuous Casting, Homogenization and Hot Extrusion Mater. Des. 152 1-9
[4]  
Wang S(2004)Novel Equilibrium Two Phase Mg Alloy With the Long-Period Ordered Structure Scr. Mater. 51 711-714
[5]  
Fan YP(2004)Long Period Stacking Structures Observed in Mg97Zn1Y2 alloy Scr. Mater. 51 107-111
[6]  
Peng QM(2016)Heat Treatment and Mechanical Properties of a High-strength cast Mg-Gd-Zn alloy Mater. Sci. Eng. A 651 745-752
[7]  
Pan JL(2009)Microstructure and Strengthening Mechanisms of a Cast Mg-1.48Gd-1.13Y-0.16Zr (at.%) Alloy J. Mater. Sci. 44 4443-4454
[8]  
Bi GL(2013)High-Strength and Good-Ductility Mg-RE-Zn-Mn Magnesium Alloy With Long-Period Stacking Ordered Phase Mater. Lett. 93 415-418
[9]  
Liu BZ(2018)Exceptional Grain Refinement in a Mg Alloy During High Pressure Torsion Due to Rare Earth Containing Nanosized Precipitates Mater. Sci. Eng. A 728 115-123
[10]  
Chen T(2017)Microstructure and Mechanical Property of a High-strength Mg–10Gd–6Y–1.5Zn–0.5Zr Alloy Prepared by Multi-Pass Equal Channel Angular Pressing J. Magnes. Alloys 5 231-259
12345678910