Surface crack propagation analysis under residual stress field

被引：0
作者：
Mochizuki M. [1 ]
Miyazaki K. [2 ]
机构：
[1] Department of Manufacturing Science, Osaka University
[2] Mechanical Engineering Research Laboratory, Hitachi, Ltd.
来源：
Welding in the World | 2006年 / 50卷 / 5-6期
关键词：
Butt joints; Comparisons; Crack propagation; Cracking; Defects; Evaluation; Fatigue tests; K1C; Mechanical tests; Plate; Practical investigations; Reference lists; Residual stresses; Strain; Stress distribution; Surfaces; Welded joints;
D O I：
10.1007/BF03266522
中图分类号：
学科分类号：
摘要：
Stress intensity factors due to surface crack propagation were analysed by using the influence function method and inherent strain analysis of the residual stress fields caused by welding. The initial residual stress in a plate with a welded butt joint was calculated by using inherent strain analysis, and the redistribution of residual stress and the stress intensity factor due to crack propagation were analysed as changes in the structure's shape. The stress intensity factor was also calculated by using an influence function database. The stress intensity factor in the residual stress fields due to crack propagation obtained by using inherent strain analysis completely agreed with that obtained by using the influence function method. The results of the crack propagation analysis were compared with the experimental results of a fatigue test. It was validated that both the inherent strain analysis and the influence function method were efficient for analysing stress intensity factors in residual stress fields caused by welding.
引用
收藏
页码：38 / 45
页数：7
相关论文
共 50 条
  • [41] Effects of Grinding Parameters on the Processing Temperature, Crack Propagation and Residual Stress in Silicon Nitride Ceramics
    Yan, Haipeng
    Deng, Fei
    Qin, Zhiying
    Zhu, Jinda
    Chang, Hongjie
    Niu, Huli
    MICROMACHINES, 2023, 14 (03)
  • [42] Behavior and Law of Crack Propagation in the Dynamic-Static Superimposed Stress Field
    Yang, Renshu
    Ding, Chenxi
    Yang, Liyun
    Zhang, Yufei
    Xu, Peng
    JOURNAL OF TESTING AND EVALUATION, 2018, 46 (06) : 2540 - 2548
  • [43] Crack Propagation Behavior and Change of Residual Stress on the Process of Bending Fatigue Test of Carburized Steel
    Ochi, Tatsuro
    Kozawa, Shuji
    Kubota, Manabu
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2011, 97 (09): : 486 - 492
  • [44] Retarding effects on crack propagation by closing crack surface using ICR treatment
    Zhiyuan, YuanZhou
    Ji Bohai
    Fu Zhongqiu
    Sun Tong
    JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2018, 143 : 11 - 17
  • [45] Ductile crack initiation and propagation of structural steels under cyclic combined shear and normal stress loading
    Jia, Liang-Jiu
    Ikai, Toyoki
    Shinohara, Kazuki
    Ge, Hanbin
    CONSTRUCTION AND BUILDING MATERIALS, 2016, 112 : 69 - 83
  • [46] Estimation Study of the Residual Stress Redistribution in Crack Propagation Process Based on Hull - Rimmer Theory
    Zhu, Lin
    Jia, Minping
    Shi, Guanglin
    INTERNATIONAL SYMPOSIUM ON MATERIALS APPLICATION AND ENGINEERING (SMAE 2016), 2016, 67
  • [47] Influence of residual stresses on the stress intensity factors for a surface crack in the rail head
    H. P. Marchenko
    Materials Science, 2010, 46 : 64 - 69
  • [48] Crack Propagation and Failure Mechanism of Modeled Recycled Concrete under Shear Stress
    Wang, Shijun
    Peng, Shengjiang
    Sun, Chang
    Singh, Amardeep
    Cheng, Ziyun
    Tian, Yunfei
    SUSTAINABILITY, 2022, 14 (09)
  • [49] Formation of the residual stress field under local thermal actions
    Burenin, A. A.
    Dats, E. P.
    Murashkin, E. V.
    MECHANICS OF SOLIDS, 2014, 49 (02) : 218 - 224
  • [50] Fatigue strength improvement by hammer peening treatment—verification from plastic deformation, residual stress, and fatigue crack propagation rate
    Masayuki Tai
    Chitoshi Miki
    Welding in the World, 2014, 58 : 307 - 318
12345