Surface crack propagation analysis under residual stress field

被引：0
|
作者：
Mochizuki M. [1 ]
Miyazaki K. [2 ]
机构：
[1] Department of Manufacturing Science, Osaka University
[2] Mechanical Engineering Research Laboratory, Hitachi, Ltd.
来源：
Welding in the World | 2006年 / 50卷 / 5-6期
关键词：
Butt joints; Comparisons; Crack propagation; Cracking; Defects; Evaluation; Fatigue tests; K1C; Mechanical tests; Plate; Practical investigations; Reference lists; Residual stresses; Strain; Stress distribution; Surfaces; Welded joints;
D O I：
10.1007/BF03266522
中图分类号：
学科分类号：
摘要：
Stress intensity factors due to surface crack propagation were analysed by using the influence function method and inherent strain analysis of the residual stress fields caused by welding. The initial residual stress in a plate with a welded butt joint was calculated by using inherent strain analysis, and the redistribution of residual stress and the stress intensity factor due to crack propagation were analysed as changes in the structure's shape. The stress intensity factor was also calculated by using an influence function database. The stress intensity factor in the residual stress fields due to crack propagation obtained by using inherent strain analysis completely agreed with that obtained by using the influence function method. The results of the crack propagation analysis were compared with the experimental results of a fatigue test. It was validated that both the inherent strain analysis and the influence function method were efficient for analysing stress intensity factors in residual stress fields caused by welding.
引用
收藏
页码：38 / 45
页数：7
相关论文
共 50 条
  • [1] Analysis of Crack Patterns Under Three-Dimensional Residual Stress Field
    Labeas, George
    Diamantakos, Ioannis
    Kermanidis, Theodoros
    ENGINEERING AGAINST FRACTURE, 2009, : 433 - 441
  • [2] Analysis of fatigue crack propagation in rails under combined action of wheel load and residual stress
    Li, Yang
    Chen, Jinjie
    Wang, Jianxi
    Chen, Long
    ENGINEERING FAILURE ANALYSIS, 2020, 115
  • [3] Fracture mechanics analysis of a crack in a residual stress field
    Y. Lei
    N.P. O'Dowd
    G.A. Webster
    International Journal of Fracture, 2000, 106 : 195 - 216
  • [4] Fracture mechanics analysis of a crack in a residual stress field
    Lei, Y
    O'Dowd, NP
    Webster, GA
    INTERNATIONAL JOURNAL OF FRACTURE, 2000, 106 (03) : 195 - 216
  • [5] Experimental investigation of fatigue crack propagation in residual stress fields
    Hensel, Jonas
    Nitschke-Pagel, Thomas
    Rebelo-Kornmeier, Joana
    Dilger, Klaus
    FATIGUE DESIGN 2015, INTERNATIONAL CONFERENCE PROCEEDINGS, 6TH EDITION, 2015, 133 : 244 - 254
  • [6] Fatigue crack propagation in threshold regime under residual stresses
    Predan, Jozef
    Pippan, Reinhard
    Gubeljak, Nenad
    INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (07) : 1050 - 1056
  • [7] Effects of the thermal residual stress field on the crack propagation in graded alumina/zirconia ceramics
    Vena, P
    Gastaldi, D
    Contro, R
    FUNCTIONALLY GRADED MATERIALS VIII, 2005, 492-493 : 177 - 182
  • [8] Effect of Compressive Residual Stress on Fatigue Crack Propagation
    Morikage, Y.
    Igi, S.
    Oi, K.
    Jo, Y.
    Murakami, K.
    Gotoh, K.
    PRESSURE VESSEL TECHNOLOGY: PREPARING FOR THE FUTURE, 2015, 130 : 1057 - 1065
  • [9] Effect of Crack Propagation on Residual Stress of Sheared Edge
    Yasutomi, Takashi
    Honda, Yoshiaki
    Sakiyama, Yuuji
    Nakata, Masahiro
    MATERIALS TRANSACTIONS, 2025, 66 (01) : 85 - 92
  • [10] Fatigue surface crack propagation and intersecting cracks in connection with welding residual stresses
    Chernyatin, A. S.
    Matvienko, Yu. G.
    Razumovsky, I. A.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2018, 41 (10) : 2140 - 2152
12345