Effect of Microstructural Banding on the Fatigue Behavior of Induction-Hardened 4140 Steel

被引：0
|
作者：
M. L. Hayne
P. I. Anderson
K. O. Findley
C. J. Van Tyne
机构：
[1] Colorado School of Mines,Department of Metallurgical and Materials Engineering
[2] The Timken Company,undefined
来源：
Metallurgical and Materials Transactions A | 2013年 / 44卷
关键词：
Fatigue; Fatigue Life; Fatigue Crack Growth; Duplex Stainless Steel; Crack Nucleation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The fatigue behavior of induction-hardened calcium-treated 4140 steel with three different case depths was evaluated using rotating bending fatigue tests. The as-received microstructure of the steel was banded and the orientation of microstructural banding with respect to the fatigue specimen was varied. Due to the inclusion shape control resulting from the calcium additions, inclusions in the steel were not elongated in the direction of the banding. It was found that microstructure banding does not have a significant influence on the fatigue properties of the steel tested. Furthermore, the fatigue limit increase with case depth is primarily related to the bending stress near the location of crack nucleation.
引用
收藏
页码：3428 / 3433
页数：5
相关论文
共 50 条
  • [41] Influence of De-icers on the Corrosion and Fatigue Behavior of 4140 Steel
    William P. Dean
    Brittain J. Sanford
    Matthew R. Wright
    Jeffrey L. Evans
    Journal of Materials Engineering and Performance, 2012, 21 : 2340 - 2344
  • [42] Metallographic study on rolling contact fatigue of 0.44%C-1.71%Mn induction-hardened bearing steels
    Choi, BY
    Shin, JH
    Bahng, GW
    Yoon, KB
    WEAR, 1996, 192 (1-2) : 1 - 5
  • [43] Effect of Surface Dent Formed by Peening on Fatigue Limit of Induction Hardened Steel with Different Hardness
    Ono K.
    Nambu K.
    Takesue S.
    Kikuchi S.
    Zairyo/Journal of the Society of Materials Science, Japan, 2023, 72 (12) : 879 - 886
  • [44] THE EFFECT OF TEMPERING TEMPERATURE ON NEAR-THRESHOLD FATIGUE CRACK BEHAVIOR IN QUENCHED AND TEMPERED 4140 STEEL
    LONDON, B
    NELSON, DV
    SHYNE, JC
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (10): : 2497 - 2502
  • [45] Effect of tempering temperature on near-treshold fatigue crack behavior in quenched and tempered 4140 steel
    London, B.
    Nelson, D.V.
    Shyne, J.C.
    Metallurgical transactions. A, Physical metallurgy and materials science, 1988, 19 A (10): : 2497 - 2502
  • [46] Investigation of the Influence Factors on Distortion in Induction-Hardened Steel Shafts Manufactured from Cold-Drawn Rod
    Dong, Juan
    Epp, Jeremy
    Rocha, Alexandre Da Silva
    Nunes, Rafael Menezes
    Zoch, Hans Werner
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2016, 47A (02): : 877 - 888
  • [47] A Study Wear Behaviour of Induction Hardened 4140 and Carburised 8617H Steels on 1040 Steel
    Kusmoko, Alain
    Crosky, Alan
    ADVANCES IN MATERIALS AND PROCESSING TECHNOLOGIES XV, 2014, 773-774 : 851 - +
  • [48] Effect of stress ratio on fatigue strength of micro pulse induction hardened steel with very thin case-hardened depth
    Ryukoku Univ, Otsu, Japan
    Zairyo/Journal of the Society of Materials Science, Japan, 1997, 46 (11): : 1242 - 1247
  • [49] Fatigue Crack Growth Behavior of Austempered AISI 4140 Steel with Dissolved Hydrogen
    Nagarajan, Varun Ramasagara
    Putatunda, Susil K.
    Boileau, James
    METALS, 2017, 7 (11):
  • [50] Effect of a thin hard chromium coating on fatigue behaviour of 4140 steel
    Ortiz-Mancilla, MJ
    Mariño-Berroterán, C
    Berríos-Ortiz, JA
    Mesmacque, G
    Puchi-Cabrera, ES
    SURFACE ENGINEERING, 2004, 20 (05) : 345 - 352
12345