Cyclic-Oxidation Behavior of Ti3Al0.7Si0.3C2 Compounds Between 900 and 1100 °C in Air

被引：1
作者：
Thuan Dinh Nguyen
Sang Whan Park
Dong Bok Lee
机构：
[1] Sungkyunkwan University,School of Advanced Materials Science and Engineering
[2] Materials Science and Technology Research Division,undefined
来源：
Oxidation of Metals | 2009年 / 72卷
关键词：
Ti; Al; Si; C; Quaternary carbide; Titanium; Aluminum; Silicon; Oxidation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Dense, monolithic Ti3Al0.7Si0.3C2 compounds were cyclically oxidized between 900 and 1100 °C in air for 100 h. Ti3Al0.7Si0.3C2 oxidized into rutile-TiO2, α-Al2O3, and amorphous SiO2, accompanied by the evaporation of carbon. Ti3Al0.7Si0.3C2 had good thermal shock resistance, so that adherent oxide scales formed, regardless of their thickness. The cyclic oxidation resistance of Ti3Al0.7Si0.3C2 was poorer than that of Ti3SiC2, Ti3AlC2, and Cr2AlC. The thermal cycling did not affect the scale morphology or the oxidation mechanism that was identified in the isothermal oxidation tests, due mainly to the formation of the adherent oxide scales.
引用
收藏
页码：299 / 309
页数：10
相关论文
共 62 条
  • [1] Barsoum MW(2000)undefined Progress in Solid State Chemistry 28 201-undefined
  • [2] Barsoum MW(1997)undefined Journal of Electrochemical Society 144 2508-undefined
  • [3] El-Raghy T(2003)undefined Journal of Electrochemical Society 150 B166-undefined
  • [4] Ogbuji LUJT(2001)undefined Corrosion Science 43 1095-undefined
  • [5] Barsoum MW(1994)undefined Journal of Materials Science 29 3384-undefined
  • [6] Ho-Duc LH(2002)undefined Metallurgical and Materials Transactions A 33 1737-undefined
  • [7] Radovic M(2002)undefined Materials Letters 55 61-undefined
  • [8] El-Raghy T(2007)undefined Oxidation of Metals 67 51-undefined
  • [9] Sun Z(2003)undefined Corrosion Science 45 891-undefined
  • [10] Zhou Y(2002)undefined Acta Materialia 50 3141-undefined
1234567