Effect of moisture on the adhesion of CFRP-to-steel bonded joints using peel tests

被引：0
|
作者：
M. M. Arouche
S. Budhe
L. A. Alves
S. Teixeira de Freitas
M. D. Banea
S. de Barros
机构：
[1] CEFET/RJ,Institut de Recherche en Génie Civil et Mécanique
[2] Federal Center of Technological Education,undefined
[3] Delft University of Technology,undefined
[4] Université de Nantes,undefined
来源：
Journal of the Brazilian Society of Mechanical Sciences and Engineering | 2018年 / 40卷
关键词：
Adhesively bonded joints; Peel tests; Moisture; CFRP; Salt water;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this work, an experimental study has been carried out to evaluate the effect of salt water condition on the long-term adhesion of composite-to-metal bonded joints using peel tests. A new test configuration is tested via fully and partially immersed specimens with 500 mm length. Fracture surfaces of non-aged samples exhibited a cohesive failure within the adhesive layer, which indicates a good adhesion of the joint. Results revealed a significant difference in the interface adhesion between aged and non-aged condition after 150 days of immersion. Partially immersed specimens allow to evaluate the adhesion performance of the joint under dry and wet condition in single specimen using a simple peel test.
引用
收藏
相关论文
共 50 条
  • [1] Effect of moisture on the adhesion of CFRP-to-steel bonded joints using peel tests
    Arouche, M. M.
    Budhe, S.
    Alves, L. A.
    Teixeira de Freitas, S.
    Banea, M. D.
    de Barros, S.
    JOURNAL OF THE BRAZILIAN SOCIETY OF MECHANICAL SCIENCES AND ENGINEERING, 2018, 40 (01)
  • [2] Influence of salt fog and ambient condition exposure on CFRP-to-steel bonded joints
    Yang, Yongming
    Zhao, Jun
    Zhang, Shishun
    Yang, Zhaohui
    Biscaia, Hugo
    COMPOSITE STRUCTURES, 2022, 280
  • [3] CFRP-to-steel bonded joints subjected to cyclic loading: An experimental study
    Yang, Yongming
    Silva, Manuel A. G.
    Biscaia, Hugo
    Chastre, Carlos
    COMPOSITES PART B-ENGINEERING, 2018, 146 : 28 - 41
  • [4] EXPERIMENTAL BEHAVIOUR OF CFRP-TO-STEEL BONDED INTERFACES
    Fernando, D.
    Yu, T.
    Teng, J. G.
    Zhao, X. L.
    PROCEEDINGS OF THE ELEVENTH INTERNATIONAL SYMPOSIUM ON STRUCTURAL ENGINEERING, VOL I AND II, 2010, : 749 - 754
  • [5] Adhesion Properties of Bonded Composite-to-Aluminium Joints Using Peel Tests
    de Freitas, Sofia Teixeira
    Sinke, Jos
    JOURNAL OF ADHESION, 2014, 90 (5-6) : 511 - 525
  • [6] Effects of elevated temperature on epoxy bonded CFRP-to-steel joints in Mode I fracture
    Jabbari, Milad
    Raftery, Gary M.
    Lim, James B. P.
    STRUCTURES, 2021, 33 : 3540 - 3549
  • [7] Environmental durability of epoxy-bonded CFRP-to-steel joints in mode I fracture
    Jabbari, Milad
    Raftery, Gary M.
    Lim, James B. P.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2022, 112
  • [8] Effect of mechanical anchorage on the bond performance of double overlapped CFRP-to-steel joints
    Yang, Yongming
    Zhao, Jun
    Zhang, Shishun
    Chastre, Carlos
    Biscaia, Hugo
    COMPOSITE STRUCTURES, 2021, 267
  • [9] Material degradation of cfrp-to-steel joints subjected to salt fog
    Yang, Yongming
    Silva, Manuel A. G.
    Silva, R. J. C.
    COMPOSITES PART B-ENGINEERING, 2019, 173
  • [10] Interface adhesion assessment of composite-to-metal bonded joints under salt spray conditions using peel tests
    Teixeira de Freitas, S.
    Banea, M. D.
    Budhe, S.
    de Barros, S.
    COMPOSITE STRUCTURES, 2017, 164 : 68 - 75
12345