Effect of Heat Input on Macro, Micro and Tensile Properties of Flux Cored Arc Welded Ferritic Stainless Steel Joints

被引：0

作者：

M. V. Venkatesan

N. Murugan

Shiju Sam

Shaju K. Albert

机构：

[1] Coimbatore Institute of Technology,Department of Mechanical Engineering

[2] Institute of Plasma Research,BTM Division

[3] Indira Gandhi Centre for Atomic Research,undefined

来源：

Transactions of the Indian Institute of Metals | 2014年 / 67卷

关键词：

Ferritic stainless steel; Flux cored arc welding; Microstructure; Macrostructure; Microhardness;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

This paper discusses the influence of Flux Cored Arc Welding Process parameters such as welding current, travel speed, voltage on bead profile, metallurgical and mechanical properties of welds of 2 mm thick 409M ferritic stainless steel sheets. The study reveals that, grain coarsening, volume fraction of martensite, hardness of heat affected zone and % of delta ferrite in ER 309 weld metal increases with increase in heat input. However, the results show that variation of heat input does not make any significant effect on tensile strength of the joint. Hence, welding parameters that provide uniform bead profile for the weld are recommended for fabrication.

引用

页码：375 / 383

页数：8

共 30 条

[1]

Taban E(2008)undefined Weld J 12 291s-undefined

[2]

Delu E(2006)undefined Weld J 11 243-undefined

[3]

Dhooge A(2002)undefined Mater Sci Eng A 329 249-undefined

[4]

Kaluc E(1999)undefined J Mater Process Technol 94 133-undefined

[5]

Greeff ML(2009)undefined Weld World 53 R199-undefined

[6]

du Toit M(2007)undefined Kovove Mater 4 67-undefined

[7]

Yamamoto K(2009)undefined Ironmak Steelmak 36 75-undefined

[8]

Kimura Y(2009)undefined J Mater Sci 43 4583-undefined

[9]

Wei FG(2009)undefined J Mater Sci Tech 25 181-undefined

[10]

Michima Y(undefined)undefined undefined undefined undefined-undefined

← 1 2 3 →