The Effect of Thermo-Mechanical Treatment on Structure of Ultrahigh Carbon PM Steel

被引:0
作者
Piotr Nikiel
Stefan Szczepanik
Stanisław Jan Skrzypek
Łukasz Rogal
机构
[1] AGH University of Science and Technology,
[2] Institute of Metallurgy and Materials Science of the Polish Academy of Sciences,undefined
来源
Journal of Materials Engineering and Performance | 2017年 / 26卷
关键词
crystallographic texture; density of lattice defects; powder metallurgy; thermo-mechanical processing; ultrahigh carbon steel; x-ray;
D O I
暂无
中图分类号
学科分类号
摘要
The effects of thermo-mechanical treatment on selected properties related to the structure of Fe-0.85Mo-0.65i-1.4C powder metallurgy (PM) steel are reported. Three kinds of initial microstructure of specimens, i.e., pearlite + ferrite + cementite, martensite + retained austenite and α + spheroidized cementite were examined. Processing was carried out on a plastometer-dilatometer Bähr machine by compression cylindrical specimens at 775 °C at a strain rate of 0.001 s−1. X-ray diffraction was carried out with symmetrical Bragg-Brentano and grazing incident angle methods on a D8-Advance diffractometer with filtered radiation of cobalt CoKα. The following features were determined: texture, density of dislocations, density of vacancies, lattice parameter of Feα and mean size of crystallites. Significant differences in structure were observed, especially in quenched specimen, as a result of the thermo-mechanical treatment. Regardless of initial state of the specimens, the determined properties were on a similar level. Crystallite size was in the range 97-106 nm, crystallite texture (I{200}/I{110}) × 10 = 1.15-1.62 and density of vacancies I{110}/I{220} = 7.06-7.52.
引用
收藏
页码:1562 / 1568
页数:6
相关论文
共 69 条
[1]  
Tsuzaki K(1999)Formation of an ( Scr. Mater. 40 675-681
[2]  
Sato E(1985) + Θ) Microduplex Structure Without Thermomechanical Processing in Superplastic Ultrahigh Carbon Steels JOM-US 37 50-56
[3]  
Furimoto S(2014)Ultrahigh Carbon Steel J. Iron. Steel Res. Int. 21 2152-2159
[4]  
Furuhara T(2012)Influence of Initial Microstructure on Warm Deformation Processability and Microstructure of an Ultrahigh Carbon Steel Mater. Sci. Eng. A 543 267-270
[5]  
Maki T(2008)Warm Deformation Behavior of Medium Carbon Steel with Different Initial Microstructures Metall. Mater. Trans. A 39A 624-635
[6]  
Sherby OD(2012)Microstructure Evolution of a Pearlitic Steel during Hot Deformation of Undercooled Austenite and Subsequent Annealing Mater. Sci. Technol. 28 116-119
[7]  
Oyama T(1993)Spheroidization behaviour of 1.0% carbon steel processed by equal channel angular extrusion and annealing JOM-US 45 40-46
[8]  
Kum DW(1994)The Case for Ultrahigh Carbon Steel as Structural Materials Metall. Mater. Trans. A 25A 1481-1493
[9]  
Walser B(1975)Influence of Microstructure on Tensile Properties of Spheroidized Ultrahigh-Carbon (1.8 Pct C) Steel Scr. Metall. 9 569-574
[10]  
Wadsworth J(2011)Superplastic UHCSs Acta Mater. 59 5787-5802