The sequence of precipitation in the Al-Mg-Si-Cu alloy AA6111

The preciptation behavior of the aluminum alloy AA6111 in the advanced stages of aging has been studied using differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and high-resolution TEM (HRTEM). The results have demonstrated the formation of various precipitate types and morphologies of quaternaryQ phase andβ (Mg2Si) families at the peak-aged condition and during overaging at different temperatures. The work has clarified the sequence ofQ phase formation and showed evidence for a new morphology of this phase. The sequence of precipitation in AA6111 is elaborated in light of the new findings.