The sequence of precipitation in the Al-Mg-Si-Cu alloy AA6111

被引：0
作者：
Xiang Wang
Shahrzad Esmaeili
David J. Lloyd
机构：
[1] McMaster University,the Department of Materials Science and Engineering
[2] University of Waterloo,the Department of Mechanical Engineering
[3] Novelis Global Technology Centre,undefined
来源：
Metallurgical and Materials Transactions A | 2006年 / 37卷
关键词：
Differential Scanning Calorimetry; Material Transaction; HRTEM; HRTEM Image; Habit Plane;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The preciptation behavior of the aluminum alloy AA6111 in the advanced stages of aging has been studied using differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and high-resolution TEM (HRTEM). The results have demonstrated the formation of various precipitate types and morphologies of quaternaryQ phase andβ (Mg2Si) families at the peak-aged condition and during overaging at different temperatures. The work has clarified the sequence ofQ phase formation and showed evidence for a new morphology of this phase. The sequence of precipitation in AA6111 is elaborated in light of the new findings.
引用
收藏
页码：2691 / 2699
页数：8
相关论文
共 77 条
[1]  
Edwards G.A.(1998)undefined Acta Mater. 46 3893-904
[2]  
Stiller K.(1998)undefined Acta Mater. 46 3283-98
[3]  
Dunlop G.L.(2001)undefined Acta Mater. 49 321-28
[4]  
Couper M.J.(2005)undefined Mater. Sci. Eng., A A390 127-38
[5]  
Anderson S.J.(2001)undefined Metall. Mater. Trans. A 32A 239-46
[6]  
Zandbergen H.W.(2002)undefined Mater. Sci. Forum 396–402 693-98
[7]  
Jansen J.(1991)undefined J. Mater. Sci. Lett. 10 323-26
[8]  
Traeholt C.(2004)undefined Acta Mater. 52 4213-47
[9]  
Turdal U.(1999)undefined Scripta Mater. 41 703-08
[10]  
Reiso O.(2000)undefined Metall. Mater. Trans. A 31A 361-71
12345678