Investigations on mechanical behaviour of dental composites

被引:0
作者
Nicoleta Ilie
Reinhard Hickel
机构
[1] Ludwig-Maximilians-University,Department of Restorative Dentistry, Dental School
来源
Clinical Oral Investigations | 2009年 / 13卷
关键词
Composites; Mechanical properties; Strength; Modulus of elasticity;
D O I
暂无
中图分类号
学科分类号
摘要
Since a direct comparison of composites efficacy in clinical studies is very difficult, our study aimed to analyse in laboratory tests under standardised and simulated clinical conditions a large variety of commercial composite materials belonging to eight different materials categories. Thus, 72 hybrid, nano-hybrid, micro-filled, packable, ormocer-based and flowable composites, compomers and flowable compomers were compared in terms of their mechanical behaviour. Flexural strength (FS), flexural modulus (FM), diametric tensile (DTS) and compressive strength (CS) were measured after the samples had been stored in water for 24 h at 37°C. Results were statistically analysed using one-way ANOVA with Tukey HSD post hoc test (α = 0.05) as well as partial η2 statistics. Large varieties between the tested materials within the same material category were found. The hybrid, nano-hybrid, packable and ormocer-based composites do not differ significantly among each other as a material type, reaching the highest FS values. Nano-hybrid composites are characterised by a good FS, the best DTS but a low FM. The lowest mechanical properties achieved the micro-filled hybrids. The flowable composites and compomers showed for all properties comparable result. Both flowable material categories do not differ significantly from the micro-filled composites for the most mechanical properties, showing only a higher DTS. The filler volume was shown to have the highest influence on the measured properties, inducing a maximum FS and FM at a level of 60%, whereas such dependence was not measured for DTS or CS. The influence of the type of material on the mechanical properties was significant but very low, showing the strongest influence on the CS.
引用
收藏
页码:427 / 438
页数:11
相关论文
共 50 条
[31]   Rheological, mechanical, and morphological behaviour of polypropylene composites reinforced with ultrafine kaolinite particles [J].
Meziane, Ouahiba ;
Bensedira, Abderrahim ;
Guessoum, Melia .
MATERIAUX & TECHNIQUES, 2024, 112 (01)
[32]   Mechanical behaviour of hard ceramic based composites obtained from SHS powders [J].
Capel, F ;
Contreras, L ;
Rodríguez, MA .
EURO CERAMICS VIII, PTS 1-3, 2004, 264-268 :1025-1028
[33]   Investigations on low-velocity ballistic impact behaviour of Kevlar / Epoxy composites reinforced with chopped wet spun fibers intruded with nanofillers [J].
Mathusoothanaperumalsukanya, Nitin ;
Sundaram, Suresh Kumar .
THIN-WALLED STRUCTURES, 2024, 198
[34]   EFFECTS OF DIFFERENT INORGANIC FILLERS ON MECHANICAL PROPERTIES AND DEGREE OF CONVERSION OF DENTAL RESIN COMPOSITES [J].
Stencel, R. ;
Pakiela, W. ;
Barszczewska-Rybarek, I ;
Zmudzki, J. ;
Kasperski, J. ;
Chladek, G. .
ARCHIVES OF METALLURGY AND MATERIALS, 2018, 63 (03) :1361-1369
[35]   Mechanical behaviour of borosilicate glass-copper composites [J].
Banuprakash, G ;
Katyal, V ;
Murthy, VSR ;
Murty, GS .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1997, 28 (9-10) :861-867
[36]   Mechanical Behaviour of Polypropylene Reinforced Palm Fibers Composites [J].
Goulart, S. A. S. ;
Oliveira, T. A. ;
Teixeira, A. ;
Mileo, P. C. ;
Mulinari, D. R. .
11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10
[37]   Mechanical behaviour of circular and triangular glass fibres and their composites [J].
Bond, I ;
Hucker, M ;
Weaver, P ;
Bleay, S ;
Haq, S .
COMPOSITES SCIENCE AND TECHNOLOGY, 2002, 62 (7-8) :1051-1061
[38]   Designing Hierarchical Honeycombs to Mimic the Mechanical Behaviour of Composites [J].
Yang, Ziyue ;
Alam, Parvez .
JOURNAL OF COMPOSITES SCIENCE, 2021, 5 (01)
[39]   Synthesis and mechanical behaviour of chlorapatite and chlorapatite/β-TCP composites [J].
Kannan, S. ;
Rebelo, A. ;
Lemos, A. F. ;
Barba, A. ;
Ferreira, J. M. F. .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2007, 27 (05) :2287-2294
[40]   The mechanical behaviour of interpenetrating phase composites - I: modelling [J].
Wegner, LD ;
Gibson, LJ .
INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2000, 42 (05) :925-942