Sintering Densification and Microstructure Formation Kinetics in Silicon Nitride Ceramics

被引：0

作者：

Igor D. Gnilitsya

机构：

[1] Ivan Franko State Oil and Gas Engineering University,

来源：

Powder Metallurgy and Metal Ceramics | 2002年 / 41卷

关键词：

silicon nitride; densification kinetics; microstructure;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Research has been done on how the shrinkage rate and microstructure in the Si3N4 ― Al2O3 ― Y2O3 are dependent on temperature and nitrogen pressure during sintering. The shrinkage rate curves alter as the activator content varies. Additional densification may occur above 1800°C because of diffusion through the increased amount of liquid.

引用

页码：360 / 365

页数：5

共 18 条

[1]

Wiederhorn S. M.(1999)Mechanisms of deformation of silicon nitride and silicon carbide at high temperatures J. Europ. Ceram. Soc. 19 2273-2284

[2]

Hockey B. J.(1997)Influence of phase transformation on grain growth rate of silicon nitride J. Ceram. Soc. Jpn. Int. Edition 105 514-516

[3]

French J. D.(1991)Consolidation and microstructure formation kinetics in a silicon nitride ceramic Repts Gov. Ind. Res. Inst., Nagoya 40 29-44

[4]

Okamoto Y.(1989)Sinter and sinter-HIP of silicon nitride ceramics with yttria and alumina additions J. Mater. Sci. 24 2047-2056

[5]

Hirosaki N.(1991)Effects of mechanical treatment and annealing on the properties of a silicon nitride ceramic Sverkhtverdye Materialy 3 33-36

[6]

Ando M.(1983)High-temperature gasostats for sintering refractory compounds Sverkhtverdye Materialy 5 12-15

[7]

Osami A.(1987)The temperature distribution in the working volume of a high-temperature gasostat at pressures up to 200 MPa Sverkhtverdye Materialy 4 11-17

[8]

Furrisa J.(undefined)undefined undefined undefined undefined-undefined

[9]

Castro F.(undefined)undefined undefined undefined undefined-undefined

[10]

Fluents M.(undefined)undefined undefined undefined undefined-undefined

← 1 2 →