Role of Al2O3 in Al2O3–Bi2O3–P2O5 glasses

被引：0
作者：
Yasser B. Saddeek
A. El-Denglawey
H. Doweidar
机构：
[1] Majmaah University,Department of Physics, College of Science in Zulfi
[2] Al-Azhar University,Physics Department, Faculty of Science
[3] Taif University,Department of Physics, College of University College at Turabah
[4] Mansoura University,Glass Research Group, Physics Department, Faculty of Science
来源：
Applied Physics A | 2021年 / 127卷
关键词：
Phosphate glasses; Bismuth oxide; Alumina; Ultrasonic velocity; Elastic moduli; FTIR;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Research on ternary Al2O3–P2O5–Bi2O3 glasses had been achieved. The changes in density and ultrasonic velocities were used to determine the elastic moduli and Debye temperature of the glasses. The investigated ultrasonic parameters were correlated with the structural variations represented by the FTIR spectra to examine the function of Al2O3 in the network of the explored glasses. It was found that the ultrasonic features are Al2O3 dependent. Inspections of FTIR spectra point that Al2O3 is preferably inserted into the phosphate network forming (AlO4) units, while Bi2O3 accesses the network as (BiO6) units merely. Moreover, the variations of the structure and the elastic moduli were inferred according to the oscillations of aluminates, bismuthate, and phosphate structural units on one side and the substitution of low-bond strength Bi2O3 via high-bond strength Al2O3. The analysis reveals the former role of Al2O3.
引用
收藏
相关论文
共 155 条
[21]  
Saddeek YB(2020)O Int. J. Appl. Glass Sci. 11 46-2340
[22]  
Mohamed GY(2005) glasses J. Non-Cryst. Solids 351 2333-614
[23]  
Shokry Hassan H(2005)Characteristic studies on Ag J. Mol. Struct. 744–747 609-531
[24]  
Mostafa AMA(2007)O-Al Opt. Quant. Electron. 39 523-165
[25]  
Abdelfadeel G(2004)O J. Non-Cryst. Solids 342 160-1559
[26]  
Tekin HO(2000)-P J. Mater. Sci. 35 1555-226
[27]  
Altunsoy EE(1997)O J. Non-Cryst. Solids 209 209-746
[28]  
Kavaz E(2002) glasses and glass ceramics J. Ram Spectrosc. 33 740-197
[29]  
Sayyed MI(1998)Glass formation in the Li J. Non-Cryst. Solids 238 193-506
[30]  
Agar O(2010)O–TiO J. Lumin. 130 498-981
12345678910