Microstructure and oxidation behaviors of near-α Ti-6.5Al-4Sn-4Zr-0.5Mo-based alloys with Ir addition

The microstructure and oxidation behaviors of near α-Ti-based alloys with small amount of iridium (Ir) additions were investigated. The microstructure of both Ir-free and Ir-containing alloys was observed to consist of α + β Widmanstätten colonies. The β lamellae gradually became continuous with increasing Ir additions since Ir acted as a β-stabilizer in the alloys. Isothermal oxidation test indicated that Ir addition reduced the oxidation resistance at 650 °C; while at 750 °C, the adherence of thermally grown oxides was enhanced, and a thin Al2O3-enriched layer on the oxide scale was promoted in the Ir-containing alloy, which suggests that Ir addition was effective in improving oxidation resistance of near-α-based alloys at 750 °C.