Improvement of Physico-mechanical Properties of Chitosan Films by Photocuring with Acrylic Monomers

Natural polymer, chitosan was obtained from dried prawn shell waste through the preparation of chitin and was characterized. Thin film of chitosan was prepared by casting method from its 2% chitosan solution. Mechanical properties like tensile strength (TS), elongation at break (Eb) of chitosan film were studied. Five formulations were developed with 2-ethyl-2-hydroxy methyl-1,3-propandiol trimethacrylate (EHMPTMA), a trifunctional monomer and 2-ethylhexyl acrylate (EHA), a monofunctional monomer in the presence of photoinitiator Darocur-1664 (2%). The film was soaked in those monomer formulations in dissimilar soaking times and irradiated under UV-radiation at different radiation intensities for the improvement of the properties of chitosan film. The cured films were then subjected to various characterization tests like TS, Eb, polymer loading (PL), water absorbency, gel content etc. The formulation, containing 25% EHMPTMA and 73% EHA showed the best performance at 10th UV passes of UV radiation for 4 min soaking time.