High pressure amplify the structural characteristic of calcium-doped Bi-2201 phase

被引：0
作者：
Yang Qi
Dalu Sun
Xingming Zhao
Bushi Dai
Yuxiang Dai
机构：
[1] Northeastern University,Department of Materials Physics and Chemistry, School of Materials Science and Engineering
[2] Northeastern University,Key Laboratory for Anisotropy and Texture of Materials, Ministry of Education
来源：
Journal of Sol-Gel Science and Technology | 2023年 / 106卷
关键词：
High-temperature superconductor; High pressure; Ca-doped Bi2201 phase; Synchrotron XRD; Raman spectroscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The experimental strategy of using pressure to amplify the influence of Ca-doping on the structure of Bi-2201 phase was proposed.Ca-doped Bi2201 crystals have smaller lattice volume, shorter c-axis, and are less compressible than the pure phase.The influence caused by the apical oxygen of the CuO6 octahedron on distortion of CuO2 plane is an important reason for increasing the Tc of the Ca-doped samples.
引用
收藏
页码：107 / 113
页数：6
相关论文
共 272 条
[1]  
Foltyn SR(2007)Materials science challenges for high-temperature superconducting wire Nat Mater 6 631-642
[2]  
Civale L(2016)Terahertz-wave emission from Bi2212 intrinsic Josephson junctions: a review on recent progress Supercond Sci Technol 29 073001-381
[3]  
MacManus-Driscoll JL(2014)Isotropic round-wire multifilament cuprate superconductor for generation of magnetic fields above 30 T Nat Mater 13 375-2129
[4]  
Jia QX(2004)Significantly enhanced critical current density in Ag-sheathed (Bi,Pb) Appl Phys Lett 84 2127-2537
[5]  
Maiorov B(2005)Sr IEEE T Appl Supercon 15 2534-4707
[6]  
Wang H(2015)Ca Adv Funct Mater 25 4700-354
[7]  
Maley M(2005)Cu Phys C 426–431 351-442
[8]  
Kakeya I(2006)O Phys C 445−448 440-95.
[9]  
Wang H(2008) composite conductors prepared by overpressure processing in final heat treatment Appl Phys Express 1 041701-169
[10]  
Larbalestier DC(2007)Controlled over pressure processing of Bi2223 long length wires. IEEE T Phys C 463−465 93-178
12345678910