Study of the physical aging of an epoxy/cycloaliphatic amine resin modified with abs

Using differential scanning calorimetry (DSC) we have studied the physical aging of an epoxy resin based on the diglycidyl ether of bisphenol A (DGEBA) modified by two different contents of an acrylonitrile-butadiene-styrene (ABS) and cured with 1,3-bisaminomethylcyclohexane (1,3-BAC). Samples fully cured were annealed at temperature of 125°C for periods of time of 72 and 120 h, to determine the process of physical aging. The apparent activation energy for the enthalpy relaxation, Dh*, is determined as the sample is heated at 10°C min-1 following cooling at various rates through the glass transition region. DSC studies suggested that the presence of thermoplastic inhibits the process of relaxation.