Synthesis and characterization of gallium-based perovskitetype dense membrane with oxygen semipermeability

被引:0
作者
You Cong
Zongping Shao
Weishen Yang
Guoxing Xiong
Liwu Lin
机构
[1] Chinese Academy of Sciences,State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics
来源
Science in China Series B: Chemistry | 2001年 / 44卷
关键词
perovskite; Ga; O; oxygen separation membrane; La; Sr; Ga; Fe; O; δ; La; Sr; Co; Fe; O; -δ;
D O I
暂无
中图分类号
学科分类号
摘要
La0.15Sr0.85Ga0.3Fe0.7O3-δ (LSGFO) and La0.15Sr0.85Co0.3Fe0.7O3-δ (LSCFO) mixed oxygenion and electron conducting oxides were synthesized by using a combined EDTA and citrate complexing method, and the corresponding dense membranes were fabricated. The properties of the oxide powders and membranes were characterized with combined SEM, XRD, H2-TPR, O2-TPD techniques, mechanical strength and oxygen permeation measurement. The results showed that LSGFO had much higher thermochemical stability than LSCFO due to the higher valence stability of Ga3+. After the temperature-programmed reduction by 5% H2 in Ar from 20°C to 1020°C, the basic perovskite structure of LSGFO was successfully preserved. LSGFO also favors the oxygen vacancy formation better than LSCFO. Oxygen permeation measurement demonstrated that LSGFO had higher oxygen permeation flux than LSCFO, but they had similar activation energy for oxygen transportation, with a value of 110 and 117 kJ · mol-1, respectively. The difference in oxygen permeation fluxes was correlated with the difference in oxygen vacancy concentrations for the two materials.
引用
收藏
页码:294 / 303
页数:9
相关论文
共 31 条
  • [1] Steele B. C. H.(1996)Ceramic ion conducting membranes Current Opinion in Solid State & Materials Science 1 684-691
  • [2] Gellings P. J.(2000)Solid-state aspects of oxidation catalysis Catal. Today 58 1-53
  • [3] Bouwmeester H. J. M.(1999)Mixed-conducting dense ceramic for gas separation application Solid-State Ionic Devices 99 61-75
  • [4] Balachandran U.(1995)Oxidative coupling of methane in a mixed-conducting perovskite membrane reactor Appl. Catal. A: General 130 195-212
  • [5] Ma B.(1997)Perovskite-type oxide membranes for the oxidative coupling of methane AIChE Journal 43 2731-2740
  • [6] Guan J.(1998)Advanced gas-to-liquids processes for syngas and liquid-phase conversion Stud. Surf. Sci. Catal. 119 867-874
  • [7] ten Elshof J. E.(1998)Ceramic membrane reactors for the conversion of natural gas to syngas Stud. Surf. Sci. Catal. 119 417-422
  • [8] Bouwmeester H. J. M.(2000)Mixed-conducting perovskite-type Sr Science in China, Series B 43 421-427
  • [9] Verweij H.(1985)Bi J. Solid State Chem. 58 257-266
  • [10] Xu S. J.(1992)FeO Solid State Ionics 52 43-56