Effect of yttria(Y2O3) coating for high temperature oxidation resistance of 9Cr-1Mo steel

被引：0

作者：

D. Ghosh

S. Mukherjee

S. Das

S. K. Mitra

机构：

[1] NDT and Metallurgy Group,Metallurgical and Materials Engineering Department

[2] CMERI,undefined

[3] National Institute of Technology,undefined

[4] National Institute of Technology,undefined

来源：

Protection of Metals and Physical Chemistry of Surfaces | 2016年 / 52卷

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

This paper investigates the effect of yttria (Y2O3) coating on high temperature oxidation behaviour of low alloy 9 Cr–1Mo steel. The superficial coating is Y2O3 was prepared for experimental investigation. The isothermal corrosion study of uncoated and coated specimens was carried out in air oxidation environment at 973 K for 8 h. The corrosion rate and reaction kinetics were studied and the post corroded scales were characterized in SEM, EDS and XRD. The results clearly indicate that Y2O3 coated specimen improves the high temperature oxidation resistance than uncoated specimens. The improvement of oxidation resistance in presence of Y2O3 coating can be attributed to the changed mechanism of scale growth from outer cation migration to inner anion migration and enhancement of scale adhesion with the substrate. Further, enhancement of scale adhesion with the substrate in case of Y2O3 coating also improves the oxidation resistance. The detail mechanism of the oxidation of Y2O3 coated and uncoated specimen is further discussed in this paper.

引用

页码：737 / 743

页数：6

共 50 条

[41] ELEVATED TEMPERATURE EROSION-CORROSION OF 9Cr-1Mo STEEL. [J].

Levy, Alan ;

Man, Yong-Fa .

1600, (111)

[42] Fracture resistances of Y2O3 particle dispersion strengthened 9Cr steel at room temperature and high temperatures [J].

Yoon, J.H. (jhyoon4@gmail.com), 1600, Korean Institute of Metals and Materials (50)

[43] Fracture Resistances of Y2O3 Particle Dispersion Strengthened 9Cr Steel at Room Temperature and High Temperatures [J].

Yoon, Ji Hyun ;

Kang, Suk Hoon ;

Lee, Yongbok ;

Kim, Sung Soo .

KOREAN JOURNAL OF METALS AND MATERIALS, 2012, 50 (01) :1-7

[44] High-Temperature corrosion and cracking of 9Cr-1Mo steel coker Tube - A case study [J].

Poorhaydari, Kioumars .

ENGINEERING FAILURE ANALYSIS, 2025, 169

[45] ELUCIDATION OF THE HIGH CYCLE FATIGUE DAMAGE MECHANISM OF MODIFIED 9CR-1MO STEEL AT ELEVATED TEMPERATURE [J].

Murakoshi, Takuya ;

Ochi, Motoyuki ;

Suzuki, Ken ;

Miura, Hideo .

PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION, 2015, VOL 9, 2016,

[46] OXIDATION BEHAVIOR OF MICROSTRUCTURALLY-DIFFERENT REGIONS IN THE WELDMENT OF 9CR-1MO STEEL [J].

RAMAN, RKS ;

LAHA, K ;

GNANAMOORTHY, JB ;

ROY, SK .

OXIDATION OF METALS, 1994, 42 (1-2) :31-48

[47] Prediction of high temperature flow stress in 9Cr-1Mo ferritic steel during hot compression [J].

Krishnan, S. A. ;

Phaniraj, C. ;

Ravishankar, C. ;

Bhaduri, A. K. ;

Sivaprasad, P. V. .

INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2011, 88 (11-12) :501-506

[48] A Creep Damage Model for High-Temperature Deformation and Failure of 9Cr-1Mo Steel Weldments [J].

Basirat, Mehdi ;

Shrestha, Triratna ;

Barannyk, Lyudmyla L. ;

Potirniche, Gabriel P. ;

Charit, Indrajit .

METALS, 2015, 5 (03) :1487-1506

[49] Effect of normalization temperatures on ductile-brittle transition temperature of a modified 9Cr-1Mo steel [J].

Chatterjee, Arya ;

Chakrabarti, D. ;

Moitra, A. ;

Mitra, R. ;

Bhaduri, A. K. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 618 :219-231

[50] Effect of sample thickness on the oxidation and carburization kinetics of 9Cr-1Mo steel in high and atmospheric pressure CO2 at 550 °C [J].

Nygren, K. E. ;

Yu, Z. ;

Rouillard, F. ;

Couet, A. .

CORROSION SCIENCE, 2020, 163

← 1 2 3 4 5 →