Effect of yttria(Y2O3) coating for high temperature oxidation resistance of 9Cr-1Mo steel

被引：0
作者：
D. Ghosh
S. Mukherjee
S. Das
S. K. Mitra
机构：
[1] NDT and Metallurgy Group,Metallurgical and Materials Engineering Department
[2] CMERI,undefined
[3] National Institute of Technology,undefined
[4] National Institute of Technology,undefined
来源：
Protection of Metals and Physical Chemistry of Surfaces | 2016年 / 52卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This paper investigates the effect of yttria (Y2O3) coating on high temperature oxidation behaviour of low alloy 9 Cr–1Mo steel. The superficial coating is Y2O3 was prepared for experimental investigation. The isothermal corrosion study of uncoated and coated specimens was carried out in air oxidation environment at 973 K for 8 h. The corrosion rate and reaction kinetics were studied and the post corroded scales were characterized in SEM, EDS and XRD. The results clearly indicate that Y2O3 coated specimen improves the high temperature oxidation resistance than uncoated specimens. The improvement of oxidation resistance in presence of Y2O3 coating can be attributed to the changed mechanism of scale growth from outer cation migration to inner anion migration and enhancement of scale adhesion with the substrate. Further, enhancement of scale adhesion with the substrate in case of Y2O3 coating also improves the oxidation resistance. The detail mechanism of the oxidation of Y2O3 coated and uncoated specimen is further discussed in this paper.
引用
收藏
页码：737 / 743
页数：6
相关论文
共 50 条
  • [21] The effects of pre-oxidation and thin Y2O3 coating on the selective oxidation of Cr18-Ni9-Ti steel
    Ma, J
    He, YD
    Wang, DR
    Gao, W
    MATERIALS LETTERS, 2004, 58 (05) : 807 - 812
  • [22] Effect of Constraint on Creep Behavior of 9Cr-1Mo Steel
    Sunil Goyal
    K. Laha
    C. R. Das
    S. Panneerselvi
    M. D. Mathew
    Metallurgical and Materials Transactions A, 2014, 45 : 619 - 632
  • [23] Effect of Y2O3 on microstructure and oxidation of chromizing coating
    Zhou Yue-bo
    Zhang Hai-jun
    Wang Yong-dong
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 (05) : 1122 - 1127
  • [24] Effect of Constraint on Creep Behavior of 9Cr-1Mo Steel
    Goyal, Sunil
    Laha, K.
    Das, C. R.
    Panneerselvi, S.
    Mathew, M. D.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (02): : 619 - 632
  • [25] Effect of Y2O3 on microstructure and oxidation of chromizing coating
    周月波
    张海军
    王永东
    TransactionsofNonferrousMetalsSocietyofChina, 2008, (05) : 1122 - 1127
  • [26] Preheat temperature of furnace tube made of 9Cr-1Mo steel
    Long, Guowen
    Chen, Boli
    Wang, Zhenjia
    Shiyou Daxue Xuebao/Journal of the University of Petroleum China, 1995, 19 (04):
  • [27] ELEVATED-TEMPERATURE EROSION CORROSION OF 9CR-1MO STEEL
    LEVY, A
    MAN, YF
    WEAR, 1986, 111 (02) : 135 - 159
  • [28] Dispersion of complex carbides at the oxidation front during the oxidation of 9Cr-1Mo steel
    Coghlan, L.
    Yan, S.
    Shin, Aya
    Pearson, J.
    Jepson, M. A. E.
    Higginson, R. L.
    CORROSION SCIENCE, 2020, 165
  • [29] Effect of variation of external stress on the oxidation behaviour of 9Cr-1Mo steel at 973 K
    Pillai, SR
    Sivaibharasi, N
    Khatak, HS
    Gnanamoorthy, JB
    CORROSION AND ITS CONTROLS, VOLS I AND II, 1998, : 878 - 884
  • [30] Effect of Addition of Boron and Nitrogen on the Corrosion Resistance of Modified 9Cr-1Mo Ferritic Steel
    Upadhyay, Namrata
    Pujar, M. G.
    Sakthivel, T.
    Mallika, C.
    Laha, K.
    Mudali, U. Kamachi
    STRUCTURAL INTEGRITY, 2014, 86 : 606 - 614
12345