Influence of Bond Coats on the Microstructure and Mechanical Behaviors of HVOF-Deposited TiAlNb Coatings

被引：0
|
作者：
H. J. Zeng
L. Q. Zhang
J. P. Lin
X. Y. He
Y. C. Zhang
P. Jia
机构：
[1] University of Science and Technology Beijing,State Key Laboratory for Advanced Metals and Materials
[2] Beijing Langqiao Surface Technology Co.,undefined
[3] Ltd.,undefined
来源：
Journal of Thermal Spray Technology | 2012年 / 21卷
关键词：
bond strength; high velocity oxygen-fuel; porosity; thermal shock test; TiAlNb intermetallic compound;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Hot dip galvanizing has been extensively employed for corrosion protection of steel structures. However, during the process of galvanization, the corrosion in molten zinc brings many problems to galvanization industry. In this study, as a material of corrosion resistance to molten zinc intended for application in Hot-dip galvanization, HVOF Ti28.15Al63.4Nb8.25Y (at.%) coatings with different bond coats (NiCr5Al, NiCoCrAlY, CoCrAlYTaSi, and NiCr80/20) were deposited onto 316L stainless steel substrate, respectively. The influences of different bond coats on HVOF Ti28.15Al63.4Nb8.25Y coatings were investigated. The results showed that bond coat had an obvious influence on improving the mechanical properties of HVOF Ti28.15Al63.4Nb8.25Y coatings. HVOF Ti28.15Al63.4Nb8.25Y coatings with NiCoCrAlY bond coat displayed the best mechanical properties. However, bond coats had no obvious effects on the microstructure, porosity, and hardness of HVOF Ti28.15Al63.4Nb8.25Y top coatings. The effects of as-received powder morphology and grain size on the characteristics of coatings were also discussed.
引用
收藏
页码：1245 / 1256
页数：11
相关论文
共 50 条
  • [1] Influence of Bond Coats on the Microstructure and Mechanical Behaviors of HVOF-Deposited TiAlNb Coatings
    Zeng, H. J.
    Zhang, L. Q.
    Lin, J. P.
    He, X. Y.
    Zhang, Y. C.
    Jia, P.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2012, 21 (06) : 1245 - 1256
  • [2] Microstructure and Mechanical Properties of TiAlNb Coating Deposited by APS and HVOF Spraying
    Zeng, Hongjie
    Zhang, Laiqi
    He, Xinyu
    Zhang, Youcha
    Jia, Pen
    Lin, Junpin
    HIGH PERFORMANCE STRUCTURE MATERIALS, 2013, 747-748 : 139 - +
  • [3] EFFECTS OF ALLOYING ELEMENTS AND SURFACE PROPERTIES ON THE CORROSION BEHAVIOR OF HVOF-DEPOSITED WC COATINGS
    Ozkan, Erhan
    MATERIALI IN TEHNOLOGIJE, 2023, 57 (03): : 291 - 298
  • [4] Influence of HVOF process parameters on microstructure and bond strength of NiCrAlY coatings
    Taheri, M.
    Valefi, Z.
    Zangeneh-Madar, K.
    SURFACE ENGINEERING, 2012, 28 (04) : 266 - 272
  • [5] Microstructure design and mechanical properties of thermal barrier coatings with layered top and bond coats
    Myoung, Sang-Won
    Kim, Jae-Hyun
    Lee, Woo-Ram
    Jung, Yeon-Gil
    Lee, Kee-Sung
    Paik, Ungyu
    SURFACE & COATINGS TECHNOLOGY, 2010, 205 (05): : 1229 - 1235
  • [6] Corrosion properties of HVOF cermet coatings with bond coats in an aqueous chloride environment
    Lekatou, A.
    Zois, D.
    Grimanelis, D.
    THIN SOLID FILMS, 2008, 516 (16) : 5700 - 5705
  • [7] Adhesion improvements of thermal barrier coatings with HVOF thermally sprayed bond coats
    Lima, C. R. C.
    Guilemany, J. M.
    SURFACE & COATINGS TECHNOLOGY, 2007, 201 (08): : 4694 - 4701
  • [8] Mechanical Properties and Microstructure of VPS and HVOF CoNiCrAlY Coatings
    S. Saeidi
    K. T. Voisey
    D. G. McCartney
    Journal of Thermal Spray Technology, 2011, 20 : 1231 - 1243
  • [9] Mechanical Properties and Microstructure of VPS and HVOF CoNiCrAlY Coatings
    Saeidi, S.
    Voisey, K. T.
    McCartney, D. G.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2011, 20 (06) : 1231 - 1243
  • [10] MECHANICAL COMPATIBILITY OF TI COATINGS DEPOSITED BY HVOF THERMAL SPRAYING
    Cutean, Elena Simona
    Mitelea, Ion
    Serban, Viorel-Aurel
    Cornea, Florin Marian
    METAL 2013: 22ND INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2013, : 1027 - 1032
12345