Laser Cladding to Improve Oxidation Behavior of Air Plasma-Sprayed Ni-20Cr Coating on Stainless Steel Substrate

被引：0
作者：
M. Mudassar Rauf
Muhammad Shahid
A. Nusair Khan
K. Mehmood
机构：
[1] National University of Sciences & Technology,School of Chemical and Material Engineering
[2] Institute of Industrial and Control System,undefined
来源：
Journal of Materials Engineering and Performance | 2015年 / 24卷
关键词：
laser; Ni-20Cr; oxidation; plasma;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Air plasma-sprayed Ni-20Cr coating on stainless steel (AISI-304) substrate was re-melted using CO2 laser to remove the inherent defects, i.e., porosity, splat boundaries, and oxides of air plasma-sprayed coating. The (1) uncoated, (2) air plasma-sprayed, and (3) laser-re-melted specimens were exposed to cyclic oxidation at 900 °C for a hundred cycles run. The oxidation products were characterized using XRD and SEM. Weight changes were determined after every 4th cycle; Uncoated samples showed severe oxidation indicated by substantial weight loss, whereas air plasma-coated samples demonstrated noticeable weight gain. However, oxidation resistance of laser-cladded samples was found to be significantly improved as the samples showed negligible weight change; porosity within the coating was minimized with an improvement in interface quality causing reduction in delamination damage.
引用
收藏
页码：3651 / 3657
页数：6
相关论文
共 64 条
[1]  
Padture NP(2002)Thermal Barrier Coatings for Gas-Turbine Engine Applications Science 296 280-284
[2]  
Gell M(2009)Mechanical Properties of Thermal Barrier Coatings After Isothermal Oxidation.: Depth Sensing Indentation Analysis Surf. Coat. Technol. 203 2307-2314
[3]  
Jordan EH(2012)Behavior of Calcia-Stabilized Zirconia Coating at High Temperature, Deposited by Air Plasma Spraying System Therm. Spray Technol. 21 121-131
[4]  
Rico A(1999)Erosion of Thermal Spray MC-Cr3C2 Cermet Coatings Wear 224 153-159
[5]  
Garcia JG(2013)Study of Ni-20Cr Coatings for High Temperature Applications Arch. Metall. Mater. 58 523-528
[6]  
Munez CJ(1997)Development and Application of High Temperature Corrosion-Resistant Materials and Coatings for Advanced Waste Energy Plants Mater. High. Temp. 14 261-268
[7]  
Poza P(2007)Characterization of Oxide Scales to Evaluate High Temperature Oxidation Behavior of Ni–20Cr Coated Superalloys Mater. Sci. Eng. A464 110-116
[8]  
Utrilla V(2010)High Temperature Corrosion Behavior of Cold Spray Ni-20Cr Coating on Boiler Steel in Molten Salt Environment at 900 °C Therm. Spray Technol. 19 110-118
[9]  
Bhatty MB(2005)Mechanical and Metallurgical Properties of Plasma Sprayed and Laser Remelted Ni–20Cr and Stellite-6 Coatings Mater. Process. Technol. 159 347-355
[10]  
Khalid FA(1993)Thermal-Shock Behaviour of Plasma-Sprayed Al Surf. Coat. Technol. 57 169-172
1234567