Optical spectroscopy of low-phonon Ho3+ doped BaY2F8 single crystal

The Ho:BaY2F8 crystal was grown by Czochralski method. The crystal phase structure and absorption spectra were tested, the absorption peak exists near 899 nm, the absorption cross section was 1.27 × 10−21 cm2. The emission spectra of crystals in the vicinity of 2 and 3.9 μm were measured, the 2 μm near infrared light induced by 5I7 → 5I8 transition of Ho3+ ions was observed, as well as the fluorescence output at 3.9 μm (5I5 → 5I6), emission cross section at 3.9 μm was calculated to be 0.86 × 10−21 cm2. We suppose that the Ho:BaY2F8 crystal has a large application prospect for the 2–4 μm wavelength near infrared laser.