Influence of ultraviolet light irradiation on the corrosion behavior of carbon steel AISI 1015

被引：0
|
作者：
H. R. Riazi
I. Danaee
M. Peykari
机构：
[1] Petroleum University of Technology,Abadan Faculty of Petroleum Engineering
来源：
Metals and Materials International | 2013年 / 19卷
关键词：
corrosion; surface; electrochemistry; scanning electron microscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Corrosion of carbon steel in sodium chloride solution was studied under ultraviolet illumination using weight loss, polarization, electrochemical impedance spectroscopy and current transient tests. The polarization test revealed an increase in the corrosion current density observed under UV illumination. The impedance spectroscopy indicated that the charge transfer resistance of the system was decreased by irradiation of UV light on a carbon steel electrode. The weight loss of carbon steel in solution increased under UV light, which confirms the results obtained from electrochemical measurements. We propose that the main effect of UV irradiation is on the oxide film, which forms on the surface. Thus, in presence of UV, the conductivity of oxide film might increase and lead to higher metal dissolution and corrosion rate.
引用
收藏
页码：217 / 224
页数：7
相关论文
共 50 条
  • [1] Influence of ultraviolet light irradiation on the corrosion behavior of carbon steel AISI 1015
    Riazi, H. R.
    Danaee, I.
    Peykari, M.
    METALS AND MATERIALS INTERNATIONAL, 2013, 19 (02) : 217 - 224
  • [2] Cinnamaldehyde as a Green Inhibitor in Mitigating AISI 1015 Carbon Steel Corrosion in HCl
    S. M. Zakir Hossain
    A. Al-Shater
    S. A. Kareem
    A. Salman
    R. A. Ali
    H. Ezuber
    M. M. Hossain
    S. A. Razzak
    Arabian Journal for Science and Engineering, 2019, 44 : 5489 - 5499
  • [3] Cinnamaldehyde as a Green Inhibitor in Mitigating AISI 1015 Carbon Steel Corrosion in HCl
    Hossain, S. M. Zakir
    Al-Shater, A.
    Kareem, S. A.
    Salman, A.
    Ali, R. A.
    Ezuber, H.
    Hossain, M. M.
    Razzak, S. A.
    ARABIAN JOURNAL FOR SCIENCE AND ENGINEERING, 2019, 44 (06) : 5489 - 5499
  • [4] Study on warm rolling of AISI 1015 carbon steel
    Medrea-Bichtas, C
    Chicinas, I
    Domsa, S
    ZEITSCHRIFT FUR METALLKUNDE, 2002, 93 (06): : 554 - 558
  • [5] Investigation of corrosion inhibition by Cassava leaf DNA on AISI 1015 low carbon steel in sodium chloride solution
    Ekere, I. E.
    Agboola, O.
    Fayomi, S. O. I.
    Ayeni, A. O.
    Ayodeji, A.
    INTERNATIONAL JOURNAL OF CORROSION AND SCALE INHIBITION, 2023, 12 (02): : 424 - 437
  • [6] Influence of ultraviolet light irradiation on corrosion behavior of weathering steel with and without TiO2-coating in 3 mass% NaCl solution
    Mahmoud, MG
    Wang, RG
    Kato, M
    Nakasa, K
    SCRIPTA MATERIALIA, 2005, 53 (11) : 1303 - 1308
  • [7] Investigations on the Corrosion-Enhanced Erosion Behavior of Carbon Steel AISI 1020
    Malik, J.
    Toor, I. H.
    Ahmed, W. H.
    Gasem, Z. M.
    Habib, M. A.
    Ben-Mansour, R.
    Badr, H. M.
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2014, 9 (12): : 6765 - 6780
  • [8] Study on mechanical properties of warm-rolled AISI 1015 carbon steel
    Medrea-Bichtas, C
    Negrea, G
    Domsa, S
    ZEITSCHRIFT FUR METALLKUNDE, 2004, 95 (03): : 176 - 178
  • [9] Influence of Rainfall on Atmospheric Corrosion Behavior of Carbon Steel
    Katayama, Hideki
    Kiyoizumi, Kota
    Shitanda, Isao
    Itagaki, Masayuki
    Tsutsumi, Yusuke
    Murase, Yoshiharu
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2021, 107 (12): : 1004 - 1010
  • [10] Influence of QPQ treatment on the Corrosion Behavior for Carbon Steel
    Sun, Fei
    Cai, Wei
    Meng, Fanna
    Hu, Jing
    MECHANICAL ENGINEERING AND GREEN MANUFACTURING II, PTS 1 AND 2, 2012, 155-156 : 922 - +
12345