Peculiarities of structure, morphology, and electrochemistry of the doped 5-V spinel cathode materials LiNi0.5-xMn1.5-yMx+yO4 (M = Co, Cr, Ti; x+y = 0.05) prepared by mechanochemical way

被引:0
作者
N. V. Kosova
I. A. Bobrikov
O. A. Podgornova
A. M. Balagurov
A. K. Gutakovskii
机构
[1] Institute of Solid State Chemistry and Mechanochemistry SB RAS,
[2] Joint Institute for Nuclear Research,undefined
[3] Rzhanov Institute of Semiconductor Physics SB RAS,undefined
[4] Novosibirsk State University,undefined
来源
Journal of Solid State Electrochemistry | 2016年 / 20卷
关键词
Doped LiNi; Mn; O; Mechanical activation; NPD; HRTEM; Electrochemical cycling; GITT;
D O I
暂无
中图分类号
学科分类号
摘要
The pure LiNi0.5Mn1.5O4 and doped spinels LiNi0.5-xMn1.5-yMx+yO4 (M = Co, Cr, Ti; x + y = 0.05) were prepared by mechanochemically assisted solid state synthesis using a high-energy AGO-2 planetary mill. The activated samples were annealed at 700 and 800 °C in oxygen and then characterized by x-ray powder diffraction (XRD) and neutron powder diffraction (NPD) with Rietveld refinement, high-resolution transmission electron microscopy (HRTEM) and electron microdiffraction, Fourier transform infrared spectroscopy (FTIR), galvanostatic cycling and galvanostatic intermittent titration technique (GITT). The structure of the high-temperature (HT) samples (800 °C) is well refined with the single Fd-3m spinel. On the contrary, the low-temperature (LT) samples (700 °C) are two-phase spinels with the 5–10 % fraction of the P4332 phase depending on the substitution ion. The dopants preferably substitute for Ni ions that correlates with the appearance of the LiyNi1-yO by-product (3–7 %). The rock salt-structured phase was observed on the surface of the particles coherently conjugated with the LT spinel crystal bulk. For all doped samples, two pairs of redox peaks are observed on the dQ/dV plots revealing the prevalence of the disordered spinel phase. However, the separation between the peaks increases for the HT samples resulting in better charge-discharge performance as compared with the undoped spinel. Lithium diffusion coefficient (DLi+) of the doped HT spinels estimated by GITT is two orders of magnitude higher than that of the undoped spinel. The highest rate capability is observed for the Ti-doped HT spinel due to larger lattice parameter.
引用
收藏
页码:235 / 246
页数:11
相关论文
共 136 条
  • [1] Santhanam R(2010)undefined J Power Sources 195 5442-5451
  • [2] Rambabu B(2010)undefined J Solid State Electrochem 14 2191-2202
  • [3] Lin GQ(2011)undefined Solid State Ion 193 32-38
  • [4] Wen L(2006)undefined Chem Mater 18 3583-3592
  • [5] Liu YM(2012)undefined Chem Mater 24 2952-2964
  • [6] Wang L(2012)undefined Chem Mater 24 3720-3731
  • [7] Li H(2004)undefined Chem Mater 16 906-914
  • [8] Huang X(2014)undefined Chem Mater 26 4377-4386
  • [9] Baudrin E(2009)undefined J Power Sources 189 752-756
  • [10] Kunduraci M(2008)undefined J Power Sources 185 1429-1433