X-ray diffraction line broadening analysis of nanostructured nickel powder

被引:0
作者
M. Bahramyan
S. Hossein Nedjad
机构
[1] Sahand University of Technology,Faculty of Materials Engineering
来源
Physics of Metals and Metallography | 2017年 / 118卷
关键词
X-ray diffraction pattern; nanostructure; dislocation structure; ball milling; nickel;
D O I
暂无
中图分类号
学科分类号
摘要
X-ray diffraction peak profile analysis is a powerful method for investigation of the microstructural characteristics of nanocrystalline materials produced by severe plastic deformation. Williamson–Hall method, its modification, and Fourier transform methods like Warren–Averbach and its modification are used to extract microstructural information based on integral breadth and Fourier coefficients of the peak profiles. In this work, pure nickel powders were milled for 2, 5, 20, and 40 h to clarify the microstructural variations for this metal with FCC atomic structure. By using the Williamson–Hall and Warren–Averbach methods and their modifications, crystallite size, microstrain, dislocation density, and character of dislocation were extracted. It was obtained that the fraction of edge-type dislocation decreased with milling time (above 50%), while after prolonged milling, the fraction of screw-type dislocations decreased, so that 50%-edge-to 50%-screw ratio was obtained. It was also found that the values of the crystallite size obtained from classical Warren–Averbach and modified Warren–Averbach (area-average) were closed.
引用
收藏
页码:839 / 845
页数:6
相关论文
共 48 条
[1]  
Ungar T.(2007)“Characterization of nanocrystalline materials by X-ray line profile analysis,” J. Mater. Sci 42 1584-1593
[2]  
Boytsov O.(2007)“Correlation between milling parameters and microstructure characteristics of nanocrystalline copper powder prepared via a high energy planetary ball mill” J. Alloy. Compd 432 103-110
[3]  
Ustinov A. I.(2013)“Structure and magnetic properties of nanostructured MnNi alloys fabricated by mechanical alloying and annealing treatments,” Phys. Met. Metallogr 114 400-405
[4]  
Gaffet E.(2004)“X-ray diffraction line profile analysis of iron ball milled powder,” Mater. Sci. Eng. A 366 229-238
[5]  
Bernard F.(2010)“Structural changes in iron powder during ball milling,” Mater. Chem. Phys 123 247-253
[6]  
Jalal T.(1953)“X-ray line broadening from filed aluminum and wolfram,” Acta Metall 1 22-31
[7]  
Hossein Nedjad S.(2011)Ahmadabadi, "X-ray diffraction study on the strain anisotropy and dislocation structure of deformed lath martensite," Metall. Mater. Trans. A 42 2493-2497
[8]  
Khalili Molan S.(2001)Crystallite size distribution and dislocation structure determined by diffraction profile analysis: principles and practical application to cubic and hexagonal crystals," J. Appl. Crystallogr 34 298-310
[9]  
Vives S.(1999)“The dislocation model of strain anisotropy in whole powder-pattern fitting: the case of a Li–Mn cubic spinel,” J.Appl. Crystallogr 32 290-295
[10]  
Gaffet E.(1998)“Dislocation, grain size and planar faults in nanostructured copper determined by high resolution X-ray diffraction and a new procedure of peak profile analysis,” Acta Mater 46 3693-3699