Influence of annealing on the structure of nanoporous oxide films on the surface of titanium‒aluminum powder alloy

被引：2

作者：

Stepanova K.V. ^{[1
]}

Yakovleva N.M. ^{[1
]}

Kokatev A.N. ^{[1
]}

Pettersson H. ^{[2
]}

机构：

[1] Petrozavodsk State University, Petrozavodsk

[2] Halmstad University, Halmstad

来源：

Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques | 2016年 / 10卷 / 5期

关键词：

annealing; anodization; crystallization; nanoporous oxide films; titanium‒aluminum powder alloy;

D O I：

10.1134/S102745101605013X

中图分类号：

学科分类号：

摘要：

Oxide films obtained during anodization of Ti‒40% Al sintered powder samples in fluorine-containing electrolytes are investigated. With scanning electron microscopy and X-ray phase analysis, it is demonstrated that an X-ray amorphous nanoporous anodic oxide film is formed on the surface of the powder microparticles under optimal anodization conditions. After annealing at T = 1093 K in air and vacuum (10‒2 Pa), the oxide films are revealed to crystallize with its regular porous structure retained. The composition of the polycrystalline anodic-oxide films annealed in air is a mixture involving TiO2 (anatase and rutile) and α- and γ-Al2O3 phases and Ti2O3 and Al2TiO5 traces. The vacuum annealing process makes it possible to identify TiO2, in which anatase is the main phase, α- and γ-Al2O3, and Ti2O3 and TiO traces. However, rutile is not revealed. The presented results indicate that the application of the anodic nanostructuring of Ti‒40% Al powders is promising for the obtainment of new photocatalytic active nanomaterials. © 2016, Pleiades Publishing, Ltd.

引用

页码：933 / 941

页数：8

共 32 条

[1]

Lai Y., Sun L., Chen Y., Zhuang H., Lin C., Chin J.W., J. Electrochem. Soc., 153, 7, (2006)

[2]

Ghicov A., Macak J.M., Tsuchiya H., Kunze J., Chem. Phys. Lett., 419, (2006)

[3]

Liu Z., Zhang X., Nishimoto S., Jin M., Tryk D.A., Murakami T., Fujishima A., J. Phys. Chem. C, 112, (2008)

[4]

Savinov E.N., Sorosovskii Obrazovat. Zh., 6, 11, (2000)

[5]

Pelaez M., Nolan N.T., Pillai S.C., Seery M.K., Et al., Appl. Catal., B, 125, (2012)

[6]

Choi J., Wehrspohn R., Gosele U., Electrochim. Acta, 50, (2005)

[7]

Nielsh K., Choi J., Schwirn K., Wehrspohn R., Gosele U., Nano Lett., 2, 7, (2002)

[8]

Sulka G.D., Highly ordered anodic porous alumina formation by self-organized anodizing and templateassisted fabrication of nanostructured materials, Nanostructured Materials in Electrochemistry, (2008)

[9]

Macak J.M., Hildebrand H., Marten-Jahns U., Schmuki P., J. Electroanal. Chem., 621, (2008)

[10]

Macak J.M., Tsuchiya H., Ghicov A., Yasuda K., Hahn R., Bauer S., Schmuki P., Curr. Opin. Solid State Mater. Sci., 11, (2007)

← 1 2 3 4 →