Casting of High-Aluminum-Content Mg Alloys Strip by a Horizontal Twin-Roll Caster

This study was aimed to investigate casting of high-aluminum-content Mg alloys strip by a horizontal twin-roll caster. A horizontal-type twin-roll caster was equipped with a nozzle. This nozzle was movable. The roll size was φ300 × W150, and copper rolls were used. The rolling road was very small. It was possible to cast AZ91D and AZ121 magnesium alloys continuously by a horizontal twin-roll caster. There was gloss and no crack. The thickness of as-cast strip of AZ91D was 4.5 mm and that of AZ121 was 4.6 mm, respectively. In the case that roll velocity was 48 m/min, the thickness of as-cast strip of AZ121 was 2.0 mm. A 2.0-mm-thick strip was able to coil, and the diameter was φ500 mm. The microstructures of the as-cast strip of AZ91D and AZ121 magnesium alloys were observed using light optical microscopy. Isometric dendrite crystals were observed at the as-cast strip. The as-cast strip without facing of AZ91D and AZ121 magnesium alloys were able to hot rolling of 75 pct reduction. The surface of the as-rolled sheet was flat and glossy. The tensile strength of the as rolled was 230 MPa and the elongation of as rolled was 4 pct.