Studies on Stress Corrosion Cracking of F304 Stainless Steel in Boiling Magnesium Chloride Solution

被引:2
作者
Pal S. [1 ]
Bhadauria S.S. [1 ]
Kumar P. [2 ]
机构
[1] Department of Industrial and Production Engineering, National Institute of Technology Jalandhar, Jalandhar
[2] Department of Mechanical Engineering, National Institute of Technology Jalandhar, Jalandhar
关键词
ASTM G36; Chloride; Corrosion; F304 Stainless steel; U Bend;
D O I
10.1007/s40735-021-00498-4
中图分类号
学科分类号
摘要
Forged (F) 304 stainless steel is well known for its material properties of corrosion resistance and can withstand in extreme environments. Hence, this study was dedicated to investigating the Stress corrosion cracking (SCC) behavior of F304 austenite stainless steel (SS) using ASTM G36. The specimen was immersed in a boiling magnesium chloride solution for 8 h, 16 h, and 24 h, respectively. The collective effect of stress and corrosion was applied with the U-bend method. The results specify the susceptibility of SCC of F304 stainless steel. Primarily, to investigate the crack initiation region, the specimen was observed after 1 h. It was found that the material was sustained only for 2 h under the boiling magnesium chloride solution. Furthermore, the Crack growth rate was calculated, and it specifies the susceptibility of F304 SS to crack initiation in the chloride environment. Similarly, the outer surface of U-bends was studied by an optical microscope to check, whether any cracks have been initiated after the SCC tests. Moreover, the hardness test and potentiodynamic polarization were performed after the exposure of boiling magnesium chloride. © 2021, The Author(s), under exclusive licence to Springer Nature Switzerland AG.
引用
收藏
相关论文
共 50 条
  • [21] Corrosion property of stainless steel surfacing layer in chloride solution
    Liu, J.-H. (hua412@126.com), 1951, Atomic Energy Press (47): : 1951 - 1955
  • [22] The Effect of Chloride-Hydrogen Sulfide Synergism on the Stress Corrosion Cracking Susceptibility of Type 321 Stainless Steel
    Ravindranath, K.
    Al-Wakaa, B.
    Tanoli, N.
    Shalaby, H. M.
    CORROSION, 2017, 73 (10) : 1268 - 1279
  • [23] LIFETIME ESTIMATION AND ACCELERATED STRESS-CORROSION CRACKING TEST OF STAINLESS-STEEL IN A NEUTRAL CHLORIDE ENVIRONMENT
    SATO, E
    ABO, H
    MURATA, T
    CORROSION, 1990, 46 (11) : 924 - 928
  • [24] Effects of Si on Stress Corrosion Cracking Properties of Austenitic Stainless Steel
    Weijia, Gong
    Shuai, Chen
    Lupeng, Liu
    Donghai, Du
    RARE METAL MATERIALS AND ENGINEERING, 2025, 54 (01) : 109 - 117
  • [25] Corrosion Behaviour of Chrome–Manganese Austenitic Stainless Steels and AISI 304 Stainless Steel in Chloride Environment
    N. N. Khobragade
    M. I. Khan
    A. P. Patil
    Transactions of the Indian Institute of Metals, 2014, 67 : 263 - 273
  • [26] Inhibitive effect of benzotriazole on the stress corrosion cracking of type 316 stainless steel in chloride and thiosulfate containing solutions
    Ashour, EA
    Hegazy, HS
    ANTI-CORROSION METHODS AND MATERIALS, 2003, 50 (04) : 291 - 295
  • [27] Antibacterial drugs as inhibitors for the corrosion of stainless steel type 304 in HCl solution
    Fouda, A. S.
    Mostafa, H. A.
    El-Abbasy, H. M.
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2010, 40 (01) : 163 - 173
  • [28] Antibacterial drugs as inhibitors for the corrosion of stainless steel type 304 in HCl solution
    A. S. Fouda
    H. A. Mostafa
    H. M. El-Abbasy
    Journal of Applied Electrochemistry, 2010, 40 : 163 - 173
  • [29] Effects of thiosulfate on susceptibility of type 316 stainless steel to stress corrosion cracking in 3.5% aqueous sodium chloride
    Ashour, EA
    Meguid, EAA
    Ateya, BG
    CORROSION, 1997, 53 (08) : 612 - 616
  • [30] The Effect of Chloride on Stress Corrosion Cracking of X100 Pipeline Steel in Carbonate/Bicarbonate Solution
    Longfei Song
    Zhiyong Liu
    Xiaogang Li
    Yue Pan
    Journal of Materials Engineering and Performance, 2022, 31 : 3763 - 3773