Thermogravimetric Investigations During the Synthesis of Silica-based MCM-41

MCM-41 material was synthesized starting from hydrogel containing colloidal fumed silica, sodium silicate, cetyltetramethylammonium bromide(CTMABr) as surfactant, and distilled water as solvent. These reactants were mixed to obtain a gel with the following composition: 4SiO2:1Na2O:1CTMABr:200H2O. The hydrogel with pH=14 was hydrothermally treated at100°C, for 4 days. Each day, the pH was measured, and then adjusted to 9.5–10 by using 30%acetic acid solution. Thermogravimetry was the main technique, which was used to monitor the participation of the surfactant on the MCM-41 nanophase, being possible to determine the temperature ranges relative to water desorption as well as the surfactant decomposition and silanol condensation.