Effect of pH on Structural and Electrical Properties of Electrodeposited Bi2Te3 Thin Films

Bi2Te3 thin films were electrodeposited at various pH values of a bismuth nitrate and tellurium oxide plating solution. Enhancement in pH results in a decrease in grain size. Transmission electron microscopy reveals the transformation of the film morphology from dispersed nanoparticles to connected chain-like nanostructures of Bi2Te3 as pH is increased. Electrical characterization for samples deposited in the temperature range of 300 K to 425 K shows a fourfold increase in Seebeck coefficient, S, between its maximum and minimum value as the solution pH changes from 1 to 3.5. Such enhancement of S is attributed to the increased connectivity of the nanostructures at higher pH.