Low-Velocity Impact Tests on Basalt Fiber/Polypropylene Core Honeycomb Sandwich Composites

被引：0
作者：
M. Bulut
机构：
[1] Hakkari University,Mechanical Engineering Department, Faculty of Engineering
来源：
Mechanics of Composite Materials | 2020年 / 56卷
关键词：
low-velocity impact; polypropylene; honeycomb; basalt fibers; failure and fracture;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The low-velocity impact behavior of polypropylene- core-based sandwich composites reinforced with basalt/epoxy facesheets was investigated by drop-weight impact tests. The impact resistance of composite samples was characterized for various impact energies according to ASTM standards. Also, the effect of facesheet thickness was explored, and the failure and fracture surfaces around the impacted region were analyzed. It was found that the thickness of facesheets played an important role in the impact properties of the honeycombs. Their residual deformation after the impact tests increased as the impact energy grew, but decreased when the number of facesheet layers increased with reducing the penetration depth and perforation.
引用
收藏
页码：121 / 130
页数：9
相关论文
共 41 条
[1]  
Chen Y(2017)Low-velocity impact response of composite sandwich structures: Modelling and experiment Compos. Struct. 168 322-334
[2]  
Hou S(2014)Low-velocity impact response of woven Kevlar/epoxy laminated composites reinforced with multi-walled carbon nanotubes at ambient and low temperatures Mater. Des. 53 152-158
[3]  
Fu K(2014)Effect of stacking sequence on failure mode of fiber metal laminates under low-velocity impact I. Iran Polym. J. 23 147-152
[4]  
Han X(2008)Failure analysis of low-velocity impact on thin composite laminates: Experimental and numerical approaches Compos. Struct. 83 413-428
[5]  
Ye L(2008)Compressive residual strength at low temperatures of composite lami­nates subjected to low-velocity impacts Compos. Struct. 85 226-232
[6]  
Taraghi I(1997)Axial crush of metallic honeycombs Int. J Impact. Eng. 19 439-56
[7]  
Fereidoon A(2017)Low-velocity bending impact behavior of foam core sandwich beams: Experimental Composites: PartE: Eng. 112 158-175
[8]  
Taheri-Behrooz F(2017)Experimental investigation of single and repeated impacts for repaired honeycomb sandwich structures Mater. Sci. Eng. A 682 23-30
[9]  
Taheri-Behrooz F(2010)Enhancement of interfacial properties of basalt fiber-reinforced nylon 6 matrix composites with silane coupling agents Exp. Polym. Lett. 4 590-598
[10]  
Shokrieh MM(2003)Static fracture and failure behavior of aligned discontinuous mineral fiber-reinforced polypropylene composites Polym. Test. 22 711-719
12345