The effect of shock-loading on the aging behavior of an Al-Mg-Si alloy

被引：0
作者：
R. S. Yassar
M. Cai
D. P. Field
X. Chen
J. Asay
机构：
[1] Washington State University,School of Mechanical and Materials Engineering
[2] Washington State University,Physics department
[3] Washington State University,Institute of Shock Physics
来源：
Journal of Materials Science | 2006年 / 41卷
关键词：
Polymer; Precipitation; Electron Microscopy; Mechanical Property; Transmission Electron Microscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The impact of pre-shock loading on the precipitation reactions in an Al-Mg-Si alloy (AA6022) was studied by means of differential scanning calorimetry (DSC), transmission electron microscopy (TEM) and hardness measurements. The samples were solutionized and quenched in water prior to subsequent shock-loading and aging treatment. The TEM and DSC results show that, while shock-loading prior to aging facilitated the precipitation of Q ′ and β, no significant effect on β′′ precipitates was observed. The hardness studies indicate that pre-shock loading strengthens the material by forming a high concentration of microstructural defects, however the resultant mechanical properties of the shocked sample are comparable to those without shock processing at the peak of aging. It was found that the rate of overaging is higher in shocked samples, which is in agreement with the DSC and TEM results.
引用
收藏
页码：1711 / 1720
页数：9
相关论文
共 50 条
  • [1] Effect of a Trace Addition of Sn on the Aging Behavior of Al-Mg-Si Alloy with a Different Mg/Si Ratio
    Ma, Lehang
    Tang, Jianguo
    Tu, Wenbin
    Ye, Lingying
    Jiang, Haichun
    Zhan, Xin
    Zhao, Jiuhui
    MATERIALS, 2020, 13 (04)
  • [2] Effect of aging time on microstructure evolution and corrosion behavior of an Al-Mg-Si alloy
    Zheng, Yaya
    Luo, Binghui
    He, Chuan
    Su, Yuelan
    MATERIALS RESEARCH EXPRESS, 2019, 6 (11):
  • [3] Influence of cold deformation on the aging behavior of the Al-Mg-Si alloy
    Aouabdia, Y.
    Amiour, L.
    Boubertakh, A.
    JOURNAL OF NEW TECHNOLOGY AND MATERIALS, 2019, 9 (02) : 28 - 34
  • [4] Nanoprecipitates and Their Strengthening Behavior in Al-Mg-Si Alloy During the Aging Process
    Li, Hui
    Liu, Wenqing
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2017, 48A (04): : 1990 - 1998
  • [5] On the effect of precipitates on the cyclic deformation behavior of an Al-Mg-Si alloy
    Jiang, Haichun
    Sandloebes, Stefanie
    Gottstein, Gunter
    Korte-Kerzel, Sandra
    JOURNAL OF MATERIALS RESEARCH, 2017, 32 (23) : 4398 - 4410
  • [6] Effect of Deep Cryogenic Treatment on Aging Processes of Al-Mg-Si Alloy
    Huang, Yuanchun
    Li, Ying
    Ren, Xianwei
    Xiao, Zhengbing
    PHYSICS OF METALS AND METALLOGRAPHY, 2019, 120 (09) : 914 - 918
  • [7] Effect of pre-aging temperature on the behavior in the early stage of aging at high temperature for Al-Mg-Si alloy
    Saga, M
    Sasaki, Y
    Kikuchi, M
    Yan, Z
    Matsuo, M
    ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 1996, 217 : 821 - 826
  • [8] Reversal of the negative natural aging effect in Al-Mg-Si alloys
    Martinsen, F. A.
    Ehlers, F. J. H.
    Torsaeter, M.
    Holmestad, R.
    ACTA MATERIALIA, 2012, 60 (17) : 6091 - 6101
  • [9] Effect of Mg and Si Content on Microstructure and Property of Al-Mg-Si Alloy
    Ren Z.
    Luo B.
    Zheng Y.
    Gao Y.
    He C.
    Cailiao Daobao/Materials Reports, 2019, 33 (09): : 3072 - 3076
  • [10] Study on Dynamic Mechanical Behavior of Al-Mg-Si Alloy
    Tao, Xiaowang
    Liu, Jibo
    Liu, Xianbin
    Chen, Jianbin
    Wang, Yonggang
    Wang, Xiaofeng
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2024, 39 (02): : 454 - 462
12345