The influence of morphology on the (hydrolytic degradation of as-polymerized and hot-drawn poly(L-lactide))

被引：0

作者：

C. A. P. Joziasse

D. W. Grijpma

J. E. Bergsma

F. W. Cordewener

R. R. M. Bos

A. J. Pennings

机构：

[1] Department of Polymer Chemistry University of Groningen Nijenborgh 4 9747 AG Groningen The Netherlands,

[2] Department od Oral and Maxillofacial Surgery University Hospital Groningen P.O. Box 30001 9700 RB Groningen The Netherlands,undefined

来源：

Colloid and Polymer Science | 1998年 / 276卷

关键词：

Key words poly(L-lactide); hydrolytic degradation; morphology; crystallinity; hot-drawn;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The influence of morpho-logy on the hydrolytic degradation behavior of poly(L-lactide) has been studied. High molecular weight and highly crystalline as-polymerized poly(L-lactide) was obtained in high yields through melt polymerization. Poly(L-lactide) fiber with a draw ratio of 5.6 was obtained by hot-drawing solution-spun fiber.