Hydration mechanism of sulphoaluminate cement

被引:0
|
作者
Zhen He
Huamei Yang
Meiyan Liu
机构
[1] Wuhan University,State Key Laboratory of Water Resources & Hydropower Engineering Science
关键词
sulphoaliminate cement; ettringite; hydration kinetics; hydration mechanism;
D O I
暂无
中图分类号
学科分类号
摘要
The feasibility of sulphoaluminate cement (SAC) utilization in support mortar was studied. Setting time and strength of as-received sulphoaluminate cement (SAC) paste were examined, hydration kinetics behavior was determined through Isothermal Calorimeter, and hydration mechanism was investigated by X-Ray diffraction analysis (XRD) and field emission scanning electron microscopy analysis (FSEM). Results showed that as-received SAC contained 61% of anhydrous calcium sulfate (3CA·CaSO4) and dicalcium silicate (C2S). The strength after 1 day or 3 days grew to 68.6% or 85.7% of that after 28 days respectively, while most of hydration heat was released within 1 day. The emergency of three exothermic peaks at acceleration stage was found and hydration kinetics model was established choosing the terminal time of the first exothermic peak at accelerating stage as the beginning of accelerating stage. XRD analysis suggested that large amount of ettringite (AFt) was produced at early age and FSEM observation revealed that ettringite (AFt) formed in sulphoaluminate cement (SAC) paste was characterized of different morphology which was proved to be caused by different ion concentrations.
引用
收藏
页码:70 / 74
页数:4
相关论文
共 50 条
  • [21] Insights into the effect mechanism of nano LiAl-LDHs on the early hydration of sulphoaluminate cement-based materials
    Haiyan Li
    Jiyou Chen
    Muhammad Moeen
    Xianping Wang
    Shuqiong Luo
    Journal of Nanoparticle Research, 2023, 25
  • [22] Insights into the effect mechanism of nano LiAl-LDHs on the early hydration of sulphoaluminate cement-based materials
    Li, Haiyan
    Chen, Jiyou
    Moeen, Muhammad
    Wang, Xianping
    Luo, Shuqiong
    JOURNAL OF NANOPARTICLE RESEARCH, 2023, 25 (04)
  • [23] Revealing the mechanism of manganese doping in sulphoaluminate cement clinker
    Wu, Qixiang
    Zhao, Ruiqi
    Sun, Yingying
    Guan, Xuemao
    Zhu, Jianping
    JOURNAL OF MOLECULAR STRUCTURE, 2024, 1301
  • [24] Accelerated Early Age Hydration of Cement Pastes Blended with Sulphoaluminate Expansive Agent
    Zeng, Luping
    Zhao, Shuang
    Wang, Wei
    Qiao, Min
    Hong, Jinxiang
    Ran, Qianping
    Wang, Yujiang
    JOURNAL OF ADVANCED CONCRETE TECHNOLOGY, 2021, 19 (06) : 655 - 667
  • [25] THE INFLUENCE OF PARTICLE SIZE OF SULPHOALUMINATE BELITE CEMENT PHASES UPON THEIR MIXTURE HYDRATION
    Palou, Martin
    Zivica, Vladimir
    Bagel, L'ubomir
    NON-TRADITIONAL CEMENT & CONCRETE IV, 2011, : 206 - +
  • [26] Effects of sulphate, calcium and aluminum ions upon the hydration of sulphoaluminate belite cement
    Palou, MT
    Majling, J
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 1996, 46 (02) : 549 - 556
  • [27] Hydration kinetics process of low alkalinity sulphoaluminate cement and its thermodynamical properties
    Zhou, Huaxin
    Liu, Jiaping
    Liu, Jianzhong
    Li, Changfeng
    2011 CHINESE MATERIALS CONFERENCE, 2012, 27 : 323 - 331
  • [28] Influence of Portland cement addition to sulphoaluminate-belite cement on hydration and mechanical properties of hardened mortars
    Janotka, I
    Krajci, L
    Mojumdar, SC
    CERAMICS-SILIKATY, 2002, 46 (03) : 110 - 116
  • [29] The influence of calcium sulphoaluminate cement on the hydration process of cement paste mixed with alkali free liquid accelerator
    Xu, Yongdong
    He, Tingshu
    Ma, Xiaodong
    Luo, Ruyi
    MATERIALS TODAY COMMUNICATIONS, 2022, 33
  • [30] Influence of the calcium sulphate source on the hydration mechanism of Portland cement-calcium sulphoaluminate clinker-calcium sulphate binders
    Pelletier-Chaignat, Laure
    Winnefeld, Frank
    Lothenbach, Barbara
    Le Saout, Gwenn
    Mueller, Christian Joerg
    Famy, Charlotte
    CEMENT & CONCRETE COMPOSITES, 2011, 33 (05): : 551 - 561