Rapid consolidation of nanostructured Ti from mechanically activated Ti and TiH2 by pulsed-current activated sintering, and the mechanical properties of the product

被引：0
作者：
Na-Ri Kim
In-Yoong Ko
Sung-Wook Cho
Wonbaek Kim
In-Jin Shon
机构：
[1] Chonbuk National University,Division of Advanced Materials Engineering, the Research Center of Advanced Materials Development
[2] Korea Institute of Geoscience,Minerals and Materials Processing Division
[3] Mining and Materials Resources,Department of Hydrogen and Fuel Cells Engineering, Specialized Graduate School
[4] Chonbuk National University,undefined
来源：
Research on Chemical Intermediates | 2011年 / 37卷
关键词：
Sintering; Nanomaterials; Hardness; Ti;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Dense nanostructured Ti was sintered from mechanically activated Ti and TiH2 powders by pulsed-current activated heating under a pressure of 80 Mpa. TiH2 powder was decomposed to Ti during sintering. The hardness of the Ti increased, and the average grain size of the Ti decreased, with increasing milling time.
引用
收藏
页码：11 / 17
页数：6
相关论文
共 49 条
[1]  
Long M(1998)undefined Biomaterials 19 1621-1639
[2]  
Rack HJ(2004)undefined Mater. Sci. Eng. 47 49-121
[3]  
Liu XY(1997)undefined Prog. Mater. Sci. 42 311-320
[4]  
Chu PK(2001)undefined Scripta Mater. 44 1061-1068
[5]  
Ding CX(1995)undefined Int. J. Refractory Met. Hard Mater 13 297-303
[6]  
Berger S(2004)undefined Mater. Sci. Eng. 383 229-234
[7]  
Porat R(2008)undefined Met. Mater. Int. 14 593-598
[8]  
Rosen R(2006)undefined Met. Mater. Int 12 141-146
[9]  
Fu L(2006)undefined Met. Mater. Int 12 393-398
[10]  
Cao LH(2009)undefined Mater. Sci. Eng. 29 1515-1520
12345