Thermally Induced Phase Transformation on 12-Tungstophosphoric Acid/ZrO2 Sol-Gel

被引：0
|
作者：
J.G. Hernández-Cortéz
T. López
M.E. Manríquez
R. Gómez
J. Navarrete
机构：
来源：
Journal of Sol-Gel Science and Technology | 2003年 / 26卷
关键词：
tungstophosphoric acid; sol-gel synthesis; ZrO; sol-gel; ZrO; NH; -TPD; FTIR pyridine adsorption on ZrO; Raman spectroscopy on sol-gel ZrO;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Zirconium (IV)-n-butoxide and tungstophosphoric acid (WP) were co-gelled at pH 3, 5 and 7 with HCl acid, C2H4O2 acid and NH4OH, respectively. Pyridine adsorption bands at 1610 and 1442 cm−1 corresponding to Lewis acidic sites were observed by FTIR spectroscopy. Acidity determined by ammonia thermodesorption shows values around 1100 μmol of NH3/g, which correspond to solids showing super acidity. It was found that the incorporation of WP to gelling zirconia delay the formation of tetragonal zirconia. Raman spectroscopy shows the stabilization of the Keggin structure on zirconia thermally treated at 400°C.
引用
收藏
页码：213 / 216
页数：3
相关论文
共 50 条
  • [21] Preparation of ZrO2 buffer layer by sol-gel methods
    Yu, Y
    Wang, XP
    Hu, XF
    JOURNAL OF INORGANIC MATERIALS, 2000, 15 (03) : 569 - 572
  • [22] ZrO2 Phase Structure in Coating Films and Powders Obtained by Sol-Gel Process
    Caruso, R.
    Pellegri, N.
    De Sanctis, O.
    Caracoche, M. C.
    Rivas, P. C.
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 1994, 3 (03) : 241 - 247
  • [23] COATING OF CARBON MATERIALS WITH ZRO2 BY SOL-GEL METHOD
    YAMAMOTO, O
    SASAMOTO, T
    INAGAKI, M
    NIPPON KAGAKU KAISHI, 1991, (10) : 1326 - 1331
  • [24] Thin ZrO2 sol-gel films for catalytic applications
    Krumov, E
    Dikova, J
    Starbova, K
    Popov, D
    Blaskov, V
    Kolev, K
    Laude, LD
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2003, 14 (10-12) : 759 - 760
  • [25] Effect of Grain Size on Phase Transformation and Photoluminescence Property of the Nanocrystalline ZrO2 Powders Prepared by Sol-Gel Method
    Chen, Qiong
    Chang, Yongqin
    Shao, Changjing
    Zhang, Jing
    Chen, Jun
    Wang, Mingwen
    Long, Yi
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2014, 30 (11) : 1103 - 1107
  • [26] Effect of Grain Size on Phase Transformation and Photoluminescence Property of the Nanocrystalline ZrO2 Powders Prepared by Sol-Gel Method
    Qiong Chen
    Yongqin Chang
    Changjing Shao
    Jing Zhang
    Jun Chen
    Mingwen Wang
    Yi Long
    JournalofMaterialsScience&Technology, 2014, 30 (11) : 1103 - 1107
  • [27] A study of the crystallization of ZrO2 in the sol-gel system:: ZrO2-SiO2
    Aguilar, DH
    Torres-Gonzalez, LC
    Torres-Martinez, LM
    Lopez, T
    Quintana, P
    JOURNAL OF SOLID STATE CHEMISTRY, 2001, 158 (02) : 349 - 357
  • [28] Phase transformation and photoluminescence properties of nanocrystalline ZrO2 powders prepared via the Pechini-type sol-gel process
    Lin, Cuikun
    Zhang, Cuimiao
    Lin, Jun
    JOURNAL OF PHYSICAL CHEMISTRY C, 2007, 111 (08): : 3300 - 3307
  • [29] δn/δT measurements of sol-gel ZrO2 thin films
    Elalamy, Z
    Drouard, E
    McGovern, T
    Escoubas, L
    Simon, JJ
    Flory, F
    ADVANCES IN OPTICAL THIN FILMS, 2003, 5250 : 278 - 285
  • [30] Investigation of sol-gel derived ZrO2 thin films by nanoindentation
    Lucca, DA
    Klopfstein, M
    Ghisleni, R
    Gude, A
    Mehner, A
    Datchary, W
    CIRP ANNALS-MANUFACTURING TECHNOLOGY, 2004, 53 (01): : 475 - 478
12345